Fabrication and evaluation of SiC/C functionally graded material

AH Wu,JT Li,CC Ge,JF Li,A Kawasaki

DOI: https://doi.org/10.3321/j.issn:1000-324X.2001.06.036

IF: 1.292

2001-01-01

Journal of Inorganic Materials

Abstract:The bulk SiC/C FGM was fabricated by powder metallurgy processing. It mixes the high erosion-resistance of Sic and high thermal-shock of graphite, and has high thermal fatigue. This work opens an application prospective for Sic ceramic.

What problem does this paper attempt to address?

Fabrication and characteristics of plasma facing SiC/C functionally graded composite material

A.H. Wu,W.B. Cao,C.C. Ge,J.F. Li,A. Kawasaki

DOI: https://doi.org/10.1016/j.matchemphys.2004.12.038

IF: 4.778

2005-06-01

Materials Chemistry and Physics

Abstract:A bulk SiC/C functionally graded material (FGM) having a compositional gradient from carbon (C) to silicon carbide (SiC) was obtained by powder metallurgy method with SiC, B and amorphous C powders as starting materials. The average graphite ratio of C was 66% higher than ordinary graphite. Compared with CVI and CVD SiC/C FGM and SiC coating, hot-pressed SiC/C FGM has high effective thermal conductivity while the thickness of SiC layer is 1mm or so. Under cyclic high-temperature heat flow conditions, SiC/C FGM did not suffer cracking and was shown to be superior in resistance to thermal fatigue. The plasma-relevant performance indicated that it has excellent high-temperature erosion resistance.

materials science, multidisciplinary
Fabrication of SiC/C Functionally Graded Material

CAO Wenbin,Wu Anhua,Li Jiangtao,Ge Changchun

DOI: https://doi.org/10.13374/j.issn1001-053x.2001.01.035

2001-01-01

Abstract:The thermal stress in SiC/C FGM in steady temperature field was analyzed based on the classical lamination theory and thermo-elastic mechanics. The optimum composition distribution parameters for fabricating SiC/C FGM were obtained through the above analysis. SiC/C FGM F4 and F7 were fabricated successfully by hot pressing. The microstructure was observed by SEM. Thermal shock resistance of SiC/C FGM was repeatedly tested by quenching from 500 ℃ into water with room temperature. It has been proved that FGM F7, which was fabricated with the optimized parameters, has better thermal shock resistance.
Design,Fabrication and Properties of SiC/C Functionally Graded Materials

Zhang Guobing,Guo Quangui,Liu Lang,Shi Jingli,Song Jinren

DOI: https://doi.org/10.3969/j.issn.1007-2330.2006.z1.014

2006-01-01

Abstract:SiC/C block Functionally graded materials(FGMs) with different layers and compositional distribution factor(P) are designed and fabricated successfully by power stacking and hot-press sintering under a pressure of 40 MPa at 2 000℃.SEM micrographs show that all SiC/C FGMs as received have excellent gradient characteristics compared with that of four-layered FGM.Gradient characteristics of eight-layered FGM have a continuous trend and its interfaces between different layers are crack-free and tightly combined.Thermal shock resistance of SiC/C FGM is repeatedly tested by water quenching with the temperature difference of 500℃.It seems that eight-layered SiC/C FGM(P=0.6) with optimized parameter has better thermal shock resistance and no cracks occur after 90 times quenching.
FABRICATION OF PLASMA FACING MATERIAL SiC/C FUNCTIONALLY GRADED MATERIAL

武安华,曹文斌,李江涛,葛昌纯

DOI: https://doi.org/10.3969/j.issn.1006-6543.2001.01.004

2001-01-01

Abstract:Hot-pressed bulk SiC/C functionally graded materials wereobtained with optimum compositions and B,C as sintering additives.SiC/C FGM hasn't cracks on surface,isn't susceptible to thermal shock.The result of irradiation on HL-1M indicates that the microstructure of SiC keeps interact and has no defects.
Processing and Characterization of Graded Sic/C Plasma Facing Composite

AH Wu,WB Cao,CC Ge,JF Li,K Akira

DOI: https://doi.org/10.3321/j.issn:1000-324x.2003.04.014

IF: 1.292

2003-01-01

Journal of Inorganic Materials

Abstract:Simultaneous sintering of SiC and C was completed with the powder metallurgical method, and with which a near dense plasma facing material with 0similar to100% compositional distributions of SiC-bulk SiC/C FGM was obtained. Well graded composition and structure of that composite were demonstrated by SEM analysis. SiC/C FGM combines the well erosion resistance of SiC and high thermal-shock resistance of graphite, and has the high effective thermal conductivity and thermal fatigue resistance. Chemical sputtering and Takamok irradiation experiments indicate that SiC/C FGM has good high temperature plasma erosion resistance.
Fabrication Of Sic/Cu Functionally Gradient Material By Graded Sintering

Yh Ling,Cg Ge,Jt Li,C Huo

2001-01-01

Abstract:SiC/Cu functionally gradient material (FGM) is a new composite that has excellent mechanical properties since it can efficiently mitigate interlayer thermal stress induced by their mismatch thermal expansion coefficients during high heat flux. It integrates the advantages of silicon carbide such as high melting point and strength, as well as copper's high heat conductivity and plasticity. Thus it exhibits satisfactory heat corrosion and thermal shock resistance and will be a prospective candidate as first-wall materials facing plasma in thermo-nuclear reactors. Due to the dramatic difference of melting point between silicon carbide and copper, conventional processes meet great difficulties in fabricating this kind of FGM. A novel approach termed graded sintering is proposed and for the first time a near dense SiC/Cu FGM that contains 0-100% compositional spectrums has been successfully fabricated. In this paper, the temperature distribution in FGM during self-resistance sintering was deduced by Fourier's heat conduction law; various means were used to characterize the sintering effects of SiC/Cu FGM, with special emphasis on relative density and microstructure analysis.
Fabrication and evaluation of SiC/Cu functionally graded material used for plasma facing components in a fusion reactor

Yun-Han Ling,Jiang-Tao Li,Chang-Chun Ge,Xin-De Bai

DOI: https://doi.org/10.1016/S0022-3115(02)00801-2

IF: 3.555

2002-01-01

Journal of Nuclear Materials

Abstract:A new SiC/Cu functionally graded material that contains a spectrum of 0–100% compositional distributions of SiC used for plasma facing component was proposed and fabricated by a novel process termed graded sintering under ultra-high pressure, by which a near dense graded composite has been successfully obtained. Tests on plasma relevant performances showed that in SiC/Cu graded composite the CD4 production due to chemical sputtering is 85% lower than that of SMF800 nuclear graphite, while its thermal desorption is about 10% of that graphite; fatigue cracks and chemical decomposition were found on the surface of SiC/Cu FGM after 300 cyclic impacts of laser pulse with power density of 398 MW/m2; slight damage was also observed on the material surface after in situ plasma irradiation in a Tokamak facility.
Fabrication of Al2O3/TiC/Ni Functionally Graded Materials by Pulsed-Electric Current Sintering and Their Mechanical Properties.

Youping Ren,Junshan Lin,Yoshinari Miyamoto,Guanjun Qiao,Zhihao Jin

DOI: https://doi.org/10.2497/jjspm.47.1205

2000-01-01

Journal of the Japan Society of Powder and Powder Metallurgy

Abstract:Dense Functionally Graded Materials (FGMs) in the systems of Al2O3/TiC/Ni and (Al2O3-WC/Co)/TiC/Ni were fabricated at 1300°C and 10 minutes by pulsed-electric current sintering method. The grain growth was effectively prevented and fine microstructure could be obtained by this rapid sintering. The residual stress produced in the outer Al2O3 and Al2O3-WC/Co layers of FGMs, which was induced by the thermal expansion mismatch between the inner TiC/Ni layer and the outer layers, was in the range of-180 MPa to-300 MPa. The compressive stress and the dispersion of WC/Co particles enhanced the toughness of the outer ceramic layers, and developed steep R-Curve behavior.
Design And Fabrication Of S-Type B4c-Sic/C Functionally Graded Materials

Weiping Shen,Bozhong Wu,Jiangtao Li,Changchun Ge

2001-01-01

Abstract:Homogeneous specimens of (I-x)(80%B4C-20%SiC)-x C (x=0,0.2,0.4,0.6,0.8) (volume fraction phi(c)) and Functionally Graded Materials were hot-pressed respectively at 2000degreesC and 20MPa under Ar atmosphere. The density, water absorption, linear thermal expansion, elastic modulus and flexural strength of the ceramics and commercial graphite were tested. Cracks were observed in FGMs of 6 and I I layers that are designed by linear function. The S-type function of compositional distribution as a design method resulted in a flexural strength of 216MPa and thermal shock resistance Delta fc > 500degreesC for the I I layered (x=0.2similar to1) FGM of S-type.
Finite Element Design of Sic/C Functionally Graded Materials for Ablation Resistance Application

Guobing Zhang,Quangui Guo,Kunjie Wang,Hua Zhang,Yan Song,Jingli Shi,Lang Liu

DOI: https://doi.org/10.1016/j.msea.2007.10.078

2008-01-01

Abstract:Elastic finite element numerical models are used to study residual thermal stresses induced during cooling from the sintering temperature of carbon-based SiC/C functionally graded materials (FGMs) for ablation resistance application. Results show that the stresses can be decreased gradually with increasing the layer number (N). In a preferred system, the optimum compositional distribution exponent (P) and thickness of intermediate graded layers and pure SiC layer are 1.0, 3.6mm and 1.0mm, respectively. On basis of the simulated results, SiC/C purpose FGM was fabricated by hot-pressing process. SEM observation shows that this material is characterized by a linearly continuous gradient in the microstructure. Further studies indicate that this material has excellent ablation and thermal shock resistances.
Development of functionally graded plasma-facing materials

Chang-Chun Ge,Jiang-Tao Li,Zhang-Jian Zhou,Wen-Bin Cao,Wei-Ping Shen,Ming-Xu Wang,Nian-Man Zhang,Xiang Liu,Zheng-Yu Xu

DOI: https://doi.org/10.1016/S0022-3115(00)00318-4

IF: 3.555

2000-01-01

Journal of Nuclear Materials

Abstract:Three different processing technologies are described for the fabrication of SiC/C functionally graded material (FGM), B4C/Cu coating FGM and W/Cu FGM. The microstructure and physical properties of the FGMs are evaluated. Some plasma-relevant performances of these three FGMs show their prospect as plasma-facing materials in fusion reactors.
Fabrication and properties of TiC/Ti3SiC2 composites and FGMs

SuiLin Shi,Wei Pan,Ruigan Wang,Yongming Luo

2003-01-01

Materials Science Forum

Abstract:Titanium silicon carbide (Ti3SiC2) is a promising ceramic material that has only been extensively studied in recent years. It combines the merits of both metals and ceramics. In this paper, TiC/Ti3SiC2 ceramic composites and functionally graded materials were fabricated and characterized sintered at 1300°C by spark plasma sintering). Physical and mechanical properties of TiC/Ti3SiC2 composites with different content of Ti3SiC2 were investigated, such as bulk density, Vickers hardness, and bending strength. All of these properties are important for the design of the functionally graded materials.
Fabrication and Properties of TiC/Ti<sub>3</sub>SiC<sub>2</sub> Composites and FGMs

Sui Lin Shi,Wei Pan,Rui Gang Wang,Yong Ming Luo

DOI: https://doi.org/10.4028/www.scientific.net/MSF.423-425.199

2003-01-01

Materials Science Forum

Abstract:Titanium silicon carbide (Ti3SiC2) is a promising ceramic material that has only been extensively studied in recent years. It combines the merits of both metals and ceramics. In this paper, TiC/Ti3SiC2 ceramic composites and functionally graded materials were fabricated and characterized sintered at 1300degreesC by spark plasma sintering). Physical and mechanical properties of TiC/Ti3SiC2 composites with different content of Ti3SiC2 Were investigated, such as bulk density, Vickers hardness, and bending strength. All of these properties are important for the design of the functionally graded materials.
Research on Sic/C Plasma-Facing Functionally Graded Materials (fgm) in China

CC Ge,WB Cao,AH Wu

DOI: https://doi.org/10.1142/9789812705198_0003

2003-01-01

Abstract:Graphite is widely used in present Tokamak facilities as first wall material and C/C composite has been selected as one of the candidate materials of diverter used in ITER. But C-based materials have too high chemical sputtering yield at 600-1000K and emerge irradiation enhanced sublimation at >1200K under the plasma erosion conditions, causing series contamination problem of plasma. SiC as a low Z advanced ceramic material, has a series of advantages for using as plasma-facing materials, however, it has relatively low thermal conductivity. Since 1997, the FGM design idea for making SiC/C plasma-facing FGM was proposed by the author and research on design and fabrication of SiC/C plasma-facing FGM was conducted in LSCPM with the aim to combine the excellent high temperature properties, low chemical sputtering, high erosion resistance, and low activation after irradiation of SiC with the high thermal conductivity of graphite, to reduce the thermal stress caused by the mismatch of thermal expansion coefficients on the interfaces and to prevent the cracks and failure under serious plasma erosion conditions. The evaluation of plasma-relevant performances was carried out in Southwest Institute of Nuclear Physics. The results of the evaluation show the good application perspective of SiC/C FGM as plasma-facing materials in fusion technology.
Design and Fabrication of TiC-based Symmetrically Compositional Functional Graded Materials

WB Cao,JT Li,CC Ge

DOI: https://doi.org/10.1016/s0261-3069(00)00043-1

2001-01-01

Materials & Design (1980-2015)

Abstract:TiC-based cermets with Ni–Mo alloys are now increasingly used in industry. For further improving the properties of TiC-based cermets with the aim to replace more kinds of WC-based cemented carbides, TiC(Mo, Ni)x/TiC(Mo, Ni)y/TiC(Mo, Ni)x symmetrically compositionally functional graded materials (SCFGM) are proposed and fabricated, which have the following advantages: (1) more wear resistant surface layers composed of less Ni–Mo alloying in combination with tougher mid-layer(s) composed of more Ni–Mo alloying; and (2) artificial residual compressive stress created on both surfaces of the specimen due to the difference in the thermal expansion coefficient between surface layers and mid-layer(s), which remarkably increases the bending strength and the fracture toughness of the SCFGM. The analytical model for SCFGM is established based on elasticity mechanics, mechanics of composite materials and computing mathematics. Triangle series are employed to describe distributions of residual thermal stress on both surfaces of the FGM caused by the difference in thermal expansion coefficients between surface layers and central layers. As an example, TiC-based SCFGM is successfully fabricated based on calculated thermal stress distribution by the self-developed SCFGM CAD system.
Investigation on the Compressive Property of SiCp/Al Functionally Gradient Materials

Li Jin,Zhou Chunling,Yang Zhichun

DOI: https://doi.org/10.3969/j.issn.1004-244X.2009.03.011

2009-01-01

Abstract:SiCp/Al functionally gradient materials reinforced with 5 μm、7 μm、10 μm SiC phase particles are fabricated respectively by powder metallurgy.The microstructure of SiCp/Al FGM specimens was observed by electron microscope(SEM);then the compression strength of SiCp/Al material is tested and its compressive properties were investigated.The results show that when the press reaches 85 kN,macroscopical shear cracks appear in the specimens of SiCp/Al FGM,and they form an angle of 45° with respect to the axial direction of the specimen.The finite element method is adopted to simulate the compress properties of SiCp/Al FGM.Simulation results show good agreement with that of compression tests.
Effect of the number of graded layers on the microstructure and properties of SiC/C functionally graded materials

G ZHANG,Q GUO,X LI,H ZHANG,Y SONG,J SHI,L LIU

DOI: https://doi.org/10.1016/j.fusengdes.2007.02.015

IF: 1.905

2007-01-01

Fusion Engineering and Design

Abstract:SiC/C bulk functionally graded materials (FGMs) with different numbers of graded layers (N) for fusion technology were designed and fabricated successfully by a power stacking method and hot-pressing process under the pressure of 30MPa at 2000°C. Results showed that the number of graded layers (N) had marked effect on the microstructure and properties of the as-received SiC/C FGMs. SEM examinations indicated that interfaces between the adjacent layers faded out gradually and became more linearly continuous gradient with increasing number of graded layers, which led to marked improvement in the bend strength and thermal shock resistance of the samples. Water quenching tests with a temperature difference of 500°C showed that SiC/C FGMs with N>8 had the best thermal shock resistance for the materials studies, and no cracks occurred after 90 quench cycles.
Preparation and Mechanical Properties of Ti 3 SiC 2 /sic Functionally Graded Materials

Yanzhi Cai,Laifei Cheng,Hongfeng Yin,Xiaowei Yin,Yangli Tian,Jinxue Chen,Nan Wang

DOI: https://doi.org/10.1016/j.ceramint.2017.02.025

IF: 5.532

2017-01-01

Ceramics International

Abstract:Ti3SiC2/SiC functionally graded materials (FGMs) were prepared via hot-pressing sintering followed by positioning impregnation. Positioning impregnation is a novel technique for local impregnation targeted at graded layers that exhibit poor sintering behaviour. The positioning impregnation process significantly densified layers with SiC volume fractions of more than 70% while only slightly affecting the densities of the other layers and preserving sufficiently weak interfaces between layers. FGMs that were hot pressed at 1600 and 1700°C and then subjected to impregnation showed not only high flexural strengths but also zigzag load-displacement behaviour. The flexural strengths of these FGMs were 436 and 485MPa, respectively; in comparison, the values for the FGMs without impregnation that were hot pressed at 1600, 1700 and 1800°C were 235, 268 and 328MPa, respectively. Moreover, the fracture toughnesses of these FGMs were 8.23 and 7.15MPam1/2, respectively; in comparison, the values for the FGMs without impregnation that were hot pressed at 1600, 1700 and 1800°C were 6.77, 7.05 and 4.65MPam1/2, respectively.
Fabrication of SiC/Al functionally graded materials via filtration extrusion

Junfeng Zhao,Zhiyu Yang,Qiulin Li,Liang Wang

DOI: https://doi.org/10.1002/adem.202300384

IF: 3.6

2023-07-20

Advanced Engineering Materials

Abstract:Functionally graded materials (FGMs) have broad application prospects owing to their outstanding material properties. In this study, a filtration extrusion device is designed, and low‐content SiC/Al composites are used to explore the feasibility of applying filtration extrusion techniques to the fabrication of FGMs. The results suggest that the extrusion force increases monotonically with an increase in the filtration extrusion ratio. Furthermore, the filtration extrusion process can be divided into two stages based on the change trend of extrusion pressure: at stage 1, extrusion force is small and increases slowly. At stage 2, the extrusion force increases significantly and rapidly. During the filtration extrusion process, the larger the initial content, the lower the extrusion temperature, the smaller the hole‐separation mold area ratio, the faster the increase in the extrusion force, and the greater the maximum extrusion force during the extrusion process. Based on filtration extrusion experiments for various extrusion distances, it is found that the transition from the non‐flow to the flow influence zone is primarily responsible for the enrichment and gradient distribution of SiC particles. The SiC particles are distributed in a gradient, and the content of SiC particles near the separation mold is higher than that on the other side. This article is protected by copyright. All rights reserved.

materials science, multidisciplinary
Processing and Properties of Functionally Graded Aluminum Matrix Composites Reinforced with Sic Particulate

FM Xu,M Qi,SJ Zhu,J Zhao,FG Wang,SX Li,ZG Wang

DOI: https://doi.org/10.3321/j.issn:0412-1961.2002.09.020

IF: 1.797

2002-01-01

ACTA METALLURGICA SINICA

Abstract:dFunctionally graded aluminum matrix composites (FGMMCs) reinforced with Sic particulate were fabricated by powder metallurgy. The microstructure and mechanical properties of the FGMMC were studied. There is no obvious interface between different layers, since Al matrix was melted together. However, the retardation of fatigue crack growth occurred from the region with high volume fraction of Sic to the low Sic regions. The retardation was explained by the analysis and observation of fracture surface and crack growth path.

Fabrication and evaluation of SiC/C functionally graded material

Fabrication and characteristics of plasma facing SiC/C functionally graded composite material

Fabrication of SiC/C Functionally Graded Material

Design,Fabrication and Properties of SiC/C Functionally Graded Materials

FABRICATION OF PLASMA FACING MATERIAL SiC/C FUNCTIONALLY GRADED MATERIAL

Processing and Characterization of Graded Sic/C Plasma Facing Composite

Fabrication Of Sic/Cu Functionally Gradient Material By Graded Sintering

Fabrication and evaluation of SiC/Cu functionally graded material used for plasma facing components in a fusion reactor

Fabrication of Al2O3/TiC/Ni Functionally Graded Materials by Pulsed-Electric Current Sintering and Their Mechanical Properties.

Design And Fabrication Of S-Type B4c-Sic/C Functionally Graded Materials

Finite Element Design of Sic/C Functionally Graded Materials for Ablation Resistance Application

Development of functionally graded plasma-facing materials

Fabrication and properties of TiC/Ti3SiC2 composites and FGMs

Fabrication and Properties of TiC/Ti<sub>3</sub>SiC<sub>2</sub> Composites and FGMs

Research on Sic/C Plasma-Facing Functionally Graded Materials (fgm) in China

Design and Fabrication of TiC-based Symmetrically Compositional Functional Graded Materials

Investigation on the Compressive Property of SiCp/Al Functionally Gradient Materials

Effect of the number of graded layers on the microstructure and properties of SiC/C functionally graded materials

Preparation and Mechanical Properties of Ti 3 SiC 2 /sic Functionally Graded Materials

Fabrication of SiC/Al functionally graded materials via filtration extrusion

Processing and Properties of Functionally Graded Aluminum Matrix Composites Reinforced with Sic Particulate