Abstract:Impact wear was carried out for annealed AISI1045 steel in this study. With the impact frequency of 600 times per min, an 8.29kN impact load was applied on the constant contact area of 540.08mm2 at the individual attack angles 60° and 90°. The microstructure of white layer for annealed AISI1045 steel was examined by SEM, TEM and HRTEM. It was found that nano structures with ferrite and cementite have been formed in white layer after impact of AISI1045 steel. Nano crystallization mechanism for ferrite is from moving, interacting and rearranging of dislocations, resulting in production of dislocation walls. With increasing strain, the density of pinned dislocations, whose Burgers vectors are usually vertical to the wall, correspondingly increases along the dislocation wall, i.e., θ/b increases. That, finally, forms subgrain boundaries with small angle θ. In addition, the density of slippery or shear-susceptible dislocations, whose Burgers vectors are often parallel to dislocation walls, also increases at the same time. The slipping of dislocations in many places along the boundary of subgrains will result in the rotation of crystals to form boundaries with large angles. Nano crystallized mechanism for cementite is mainly due to shearing fracture, neck-like shrinkage fracture and carbides dissolving under the impact. The cementite thinning and the formation of slipping stages will increase the surface energy per volume, which causes the dissolution of cementite. The chemical potential energy difference between carbon atoms and cementite is a driver for dissolving cementite. The moving, reacting and proliferating of dislocations promote carbon atoms diffusing and migrating to distant ferrite from the boundary of cementite, which accelerates the dissolution of cementite.

Formation of Nanocrystallized Structure in Worn Surface Layer of T10 Steel Against 20crmnti Steel During Dry Rubbing

Formation of sliding friction-induced deformation layer with nanocrystalline structure in T10 steel against 20CrMnTi steel

Strain-induced Refinement and Thermal Stability of a Nanocrystalline Steel Produced by Surface Mechanical Attritiontreatment

Atomic diffusion of gradient ultrafine structured surface layer produced by T10 steel rubbing against 20CrMnTi steel

Subsurface Dynamic Deformation and Nano-structural Evolution in 40cr Steel under Dry Sliding Wear

Cr atom diffusion in tribolayer T10 steel induced by dry sliding against 20CrMnTi steel

Influence mechanism of grinding surface quality of 20CrMnTi steel on contact failure

Microstructure Transformation in the Worn Surface Layer of Austenite-Bainite Steel with Nodular Eutectics during Impact Wear

Effect of Ultrasonic Nanocrystalline Surface Modification Process on Fretting Wear Behavior of Laser Surface Textured 20crmoh Steel

Sliding Friction Induced Atom Diffusion in the Deformation Layer of 0.45% C Steel Rubbed Against Tin Alloy

Surface self-nanocrystallization and -lubricating dependent wear resistance of austenitic steels at same initial hardness level

Structural Transformations and Tribological Effects in the Surface Layer of Austenitic Chrome-Nickel Steel Initiated by Nanostructuring and Oxidation

Frictional Hardening and Softening of Steel 52100 During Dry Sliding

Wear behaviour of nanocrystallised Hadfield steel

Evolution of Wear Damage in Gross Sliding Fretting of a Nitrided High-Carbon High-Chromium Steel

Investigation on triboelectrification behavior of surface nanocrystallization of medium carbon steel

Mechanisms of remarkable wear reduction and evolutions of subsurface microstructure and nano-mechanical properties during dry sliding of nano-grained Ti6Al4V alloy: A comparative study

Sliding Friction Surface Microstructure and Wear Resistance of 9sicr Steel with Low-Temperature Austempering Treatment

Mechanisms of near-surface structural evolution in nanocrystalline materials during sliding contact

Nano Structure and Transformation Mechanism of White Layer for Aisi1045 Steel During Impact Wear

Grain coarsening of nano laminated structure in martensite steel under sliding wear