Research on mechanical properties of duplex stainless steel S22053 at elevated temperature and after fire
Tiancheng Chen,Shenggang Fan,Qingfeng Xu,Kuiyuan Xu,Jinpeng Luo,Yuxian Tang
DOI: https://doi.org/10.1016/j.tws.2024.111620
IF: 5.881
2024-02-02
Thin-Walled Structures
Abstract:Stainless steel has advantages such as corrosion resistance, durability and esthetic appearance, with extensive application prospects in the field of construction engineering . In order to investigate the mechanical properties of duplex stainless steel S22053 at elevated temperature and after fire, 58 standard coupons were fabricated, with 4 coupons for tensile tests at ambient temperature, 18 coupons for steady-state tests at elevated temperatures, and 36 coupons for tensile tests after fire. The temperatures were set at 100 °C, 200 °C, 300 °C, 400 °C, 500 °C, 600 °C, 700 °C, 800 °C and 900 °C, in total of 9 temperature levels. Two cooling methods, water cooling and air cooling, were employed for the postfire coupons. Based on the test results, the expressions of stress-strain relations for duplex stainless steel S22053 under two fire conditions were proposed, and comparisons were made with existing models. The reduction formulas for 6 major mechanical parameters ( E 0 , σ 0.05 , σ 0.2 , σ 1.0 , σ 2.0 and σ u ) of duplex stainless steel S22053 under two fire conditions were obtained through data fitting. Reliability analysis was performed on the mechanical property parameters, and corresponding standard values were proposed.
engineering, mechanical,mechanics, civil