Abstract:Amorphous hydrous ruthenium oxide/active carbon (RuO2. xH(2)O/C) powders were prepared by a simple procedure based on the sol-gel process. The precursor was obtained by mixing an aqueous solution of RuCl3 and active carbon powders at pH 7. When annealing the precursor at 150 degreesC for 7-9.5 h, the RuO2. xH(2)O/C powders obtained had the highest specific capacitance. Transmission electron microscopy photographs showed that the RuO2. xH(2)O primary particles were about 10-15 nm diam. They adhered to form large porous secondary particles. A modeling capacitor was made with electrodes comprised of RuO2. xH(2)O/C powder and 30% H2SO4 electrolyte. At 10-20 wt % ruthenium in the electrodes, the specific capacitance remained almost unchanged at 243 F/g, which included both the electric double-layer capacitance associated with the high surface area of active carbon and redox capacitance associated with ruthenium oxide. About 52% of the RuO2 in the RuO2. xH(2)O/C powders was utilized. More than 50% of the capacitance in the electrode with 12.1% ruthenium was due to the formation of the double layer, but for the electrode with 21.1% ruthenium, the capacitance attributed to the double layer dropped to 16.8% of the total capacitance. When the electrodes contained ruthenium from 35 wt % to pure RuO2. xH(2)O, the specific capacitance increased from 350 to 715 F/g. The specific capacitance was proportional to the mass of the ruthenium in the electrodes. This enabled the specific capacitance to be controlled by changing the mass ratio of RuCl3 to active carbon in the preparation. Physical properties of the material and electrochemical characteristics of electrodes are also reported along with the capacitor performance. (C) 2001 The Electrochemical Society.

Activated Carbon Based Ruthenium Oxide Materials For Supercapacitor

Preparation And Electrochemistry Of Hydrous Ruthenium Oxide/Active Carbon Electrode Materials For Supercapacitor

Electrochemical Performance of RuO2/Active Carbon Composite Electrodes

Electrochemical Behavior Of Amorphous Hydrous Ruthenium Oxide/Active Carbon Composite Electrodes For Super-Capacitor

Carbon Nanotube Capacitor Materials Loaded with Different Amounts of Ruthenium Oxide

Nano ruthenium oxide/carbon nanotubes composite electrode material for electrochemical capacitors

Supercapacitor electrode materials of nanostructured hydrous ruthenium oxide deposited by cyclic voltammetry method

Pseudo-capacitance of ruthenium oxide/carbon black composites for electrochemical capacitors

Ultra-Fine Ruthenium Oxide Quantum Dots/Reduced Graphene Oxide Composite as Electrodes for High-Performance Supercapacitors

Hydrous–ruthenium–oxide thin film electrodes prepared by cathodic electrodeposition for supercapacitors

Hydrous Ruthenium Oxide with High Rate Pseudo-Capacitance Prepared by a New Sol-Gel Process

High-performance Supercapacitors of Hydrous Ruthenium Oxide/mesoporous Carbon Composites

Supercapacitive Properties Of Hydrous Ruthenium Oxide/Multi-Walled Carbon Nanotubes Nanocomposite

Investigation of the supercapacitance of ruthenium-based/ hemp stem activated carbon

Mesoporous Transition Metal Oxides for Supercapacitors.

A Hybrid Metal Oxide Supercapacitor in Aqueous KOH Electrolyte†

On the Utilization of Supercapacitor Electrode Materials

Co2SnO4/activated Carbon Composite Electrode for Supercapacitor

Porous α-Fe2O3 Hollow Rods/Reduced Graphene Oxide Composites Templated by MoO3 Nanobelts for High-Performance Supercapacitor Applications

Hydrothermal Synthesis of CuO/RuO2/MWCNT Nanocomposites with Morphological Variants for High Efficient Supercapacitors

A pH-Tailored Anodic Deposition of Hydrous RuO2 for Supercapacitors