Abstract:Amorphous hydrous ruthenium oxide/active carbon (RuO2. xH(2)O/C) powders were prepared by a simple procedure based on the sol-gel process. The precursor was obtained by mixing an aqueous solution of RuCl3 and active carbon powders at pH 7. When annealing the precursor at 150 degreesC for 7-9.5 h, the RuO2. xH(2)O/C powders obtained had the highest specific capacitance. Transmission electron microscopy photographs showed that the RuO2. xH(2)O primary particles were about 10-15 nm diam. They adhered to form large porous secondary particles. A modeling capacitor was made with electrodes comprised of RuO2. xH(2)O/C powder and 30% H2SO4 electrolyte. At 10-20 wt % ruthenium in the electrodes, the specific capacitance remained almost unchanged at 243 F/g, which included both the electric double-layer capacitance associated with the high surface area of active carbon and redox capacitance associated with ruthenium oxide. About 52% of the RuO2 in the RuO2. xH(2)O/C powders was utilized. More than 50% of the capacitance in the electrode with 12.1% ruthenium was due to the formation of the double layer, but for the electrode with 21.1% ruthenium, the capacitance attributed to the double layer dropped to 16.8% of the total capacitance. When the electrodes contained ruthenium from 35 wt % to pure RuO2. xH(2)O, the specific capacitance increased from 350 to 715 F/g. The specific capacitance was proportional to the mass of the ruthenium in the electrodes. This enabled the specific capacitance to be controlled by changing the mass ratio of RuCl3 to active carbon in the preparation. Physical properties of the material and electrochemical characteristics of electrodes are also reported along with the capacitor performance. (C) 2001 The Electrochemical Society.

Supercapacitive Properties Of Hydrous Ruthenium Oxide/Multi-Walled Carbon Nanotubes Nanocomposite

Carbon Nanotube Capacitor Materials Loaded with Different Amounts of Ruthenium Oxide

High-performance Supercapacitors of Hydrous Ruthenium Oxide/mesoporous Carbon Composites

Nano ruthenium oxide/carbon nanotubes composite electrode material for electrochemical capacitors

Hydrothermal Synthesis of CuO/RuO2/MWCNT Nanocomposites with Morphological Variants for High Efficient Supercapacitors

Electrochemical Behavior Of Amorphous Hydrous Ruthenium Oxide/Active Carbon Composite Electrodes For Super-Capacitor

Preparation And Electrochemistry Of Hydrous Ruthenium Oxide/Active Carbon Electrode Materials For Supercapacitor

Supercapacitor electrode materials of nanostructured hydrous ruthenium oxide deposited by cyclic voltammetry method

The Supercapacitive Properties of Ni-Ru Oxide Composites

Preparation and Electrochemical Properties of Multiwalled Carbon Nanotubes–nickel Oxide Porous Composite for Supercapacitors

High-rate supercapacitor utilizing hydrous ruthenium dioxide nanotubes

Pseudo-capacitance of ruthenium oxide/carbon black composites for electrochemical capacitors

Improved Supercapacitive Performance Based on Novel RuO2/ 2 / SiO2 2 Nanocomposites

Preparation and Electrochemical Capacitance of RuO2/TiO2 Nanotubes Composites

Activated Carbon Based Ruthenium Oxide Materials For Supercapacitor

Fabrication and Supercapacitive Properties of a Thick Electrode of Carbon Nanotube–ruo2 Core–shell Hybrid Material with a High RuO2 Loading

Hydrous Ruthenium Oxide with High Rate Pseudo-Capacitance Prepared by a New Sol-Gel Process

Enhanced Electrochemical Performance of Hydrous RuO2/mesoporous Carbon Nanocomposites Via Nitrogen Doping.

Formation and Characterization of Multi-Walled Carbon Nanotubes/co3o4 Nanocomposites for Supercapacitors

Enhanced Electrochemical Performance of Mn3O4/Multiwalled Carbon Nanotube Nanocomposite for Supercapacitor Applications

Investigation of the supercapacitance of ruthenium-based/ hemp stem activated carbon