Preparation of Sb2O3/Sb2S3/FeOOH Composite Photoanodes for Enhanced Photoelectrochemical Water Oxidation

Yang Peng,Jia Chen,Liang-xing Jiang,Tian-yi Wang,Hai-chao Yang,Fang-yang Liu,Ming Jia
DOI: https://doi.org/10.1016/s1003-6326(20)65325-0
IF: 3.752
2020-01-01
Transactions of Nonferrous Metals Society of China
Abstract:A novel Sb2O3/Sb2S3/FeOOH photoanode was fabricated via a simple solution impregnation method along with chemical bath deposition and post-sulfidation. The X-ray diffractometry, Raman measurement, and X-ray photoelectron spectroscopy show that the Sb2O3/Sb2S3/FeOOH thin films are successfully prepared. SEM?EDS analyses reveal that the surface of Sb2O3/Sb2S3 thin films becomes rough after the immersion in the FeCl3 solution. The optimized impregnation time is found to be 8 h. The FeOOH co-catalyst loaded Sb2O3/Sb2S3 electrode exhibits an enhanced photocurrent density of 0.45 mA/cm2 at 1.23 V versus RHE under simulated 1 sun, which is approximately 1.41 times compared to the photocurrent density of the unloaded one. Through the further tests of UV?Vis spectroscopy, the electrochemical impedance spectra, and the PEC measurements, the enhancement can result from the increased light-harvesting ability, the decreased interface transmission impedance, and the remarkably enhanced carrier injection efficiency.
What problem does this paper attempt to address?