Abstract:This study investigated the effect of the synergistic addition of Gd and Mn on the microstructure and mechanical properties of extruded Mg-1Bi alloys. The grain size of an Mg-1Bi alloy decreased sharply when either only Gd or Mn was added to the alloy, whereas a strong grain refining effect was verified upon the co-addition of Gd and Mn. The Mg-1Bi and Mg-1Bi-0.4Mn alloys exhibited typical strong basal textures, whereas the Mg-1Bi-0.3Gd and Mg-1Bi-0.3Gd-0.6Mn alloys showed weakened extrusion direction (ED)-split textures. The weakened ED-split texture leads to a high average Schmid factor for basal slip (SF b ). Higher SF b for the sheet exhibited the lower yield strength and higher ductility. Furthermore, the synergistic addition of Gd and Mn resulted in considerably higher strength and ductility than the addition of either Gd or Mn alone. The Mg-1Bi-0.3Gd-0.6Mn sheet shows the ultimate tensile and yield strengths of ~ 275.6 and ~ 180.2 MPa along the transverse direction (TD) and ~ 273.2 and ~ 155.4 MPa along the extrusion direction (ED), respectively. Moreover, the elongation of Mg-1Bi-0.3Gd-0.6Mn sheet along the TD and ED increased to ~ 7.3 and ~ 7.5%, respectively, more than two times compared with the corresponding values for the Mg-1Bi sheet. The increased yield strength of the Mg-1Bi-0.3Gd-0.6Mn sheet was mainly attributed to the effect of refined grain size, fine α-Mn and MgBiGd particles, and the Gd solute. In addition, the ductility of the Mg-1Bi-0.3Gd-0.6Mn sheet was substantially increased because of the fine grain size and weak texture having a high average SF b .

Influence of Ca and Zn Synergistic Alloying on the Microstructure, Tensile Properties and Strain Hardening of Mg-1Gd Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Influences of Gd on the Microstructure and Strength of Mg–4.5Zn Alloy

Influence of Zn on the microstructure and mechanical properties of Mg-Gd-Zr alloy

Microstructure and Mechanical Properties of Extruded Mg–Zn–Mn–Ca Alloys

Effects of Alloying Elements on the Microstructure and Mechanical Properties of Mg-Zn-Gd Alloys

Simultaneous improvement of strength and ductility by Mn addition in extruded Mg–Gd–Zn alloy

The Role of Ca on the Microstructure and Tensile Properties of Mg-Al-Zn-Ca Alloys

Effects of Zn Addition on the Microstructure, Tensile Properties and Formability of As-Extruded Mg-1Sn-0.5Ca Alloy

Microstructures and Mechanical Properties of the Mg–4.5Zn–xGd (x = 0, 2, 3 and 5) Alloys

Effects of Mn Addition on the Microstructures and Mechanical Properties of the Mg-15Gd-1Zn Alloy

The effects of Ca and Mn on the microstructure, texture and mechanical properties of Mg-4 Zn alloy

Effects of Zn addition on microstructures and mechanical properties of as-extruded Mg-Zn-Ce-Zr alloys

A good balance between strength and ductility in Mg–Zn–Mn-Gd alloy

Improving tensile properties and corrosion resistance of Mg–Zn–Ca–Mn alloy via Gd addition

Effects of Zn and Gd Contents and Their Ratios on Microstructure and Mechanical Properties of As-Cast and As-Extruded Mg−8Li Alloys

Effects of the Simultaneous Addition of Gd and Mn on the Microstructures and Mechanical Properties of Mg-Bi Alloys

The balance between work hardening and softening behaviors of Mg-xZn-1Gd-0.2Ca-0.1Zr alloys influenced by trace Zn addition

Effect of Ca Concentration on Microstructure and Mechanical Properties of As-Cast and As-Extruded Quasicrystal-Strengthened Mg-7.2Zn-2.4Gd Alloy

Achieving high strength above 400 MPa in conventionally extruded Mg-Ca-Zn ternary alloys

Effect of Zn/(Gd+Y) ratio on the microstructure evolution and mechanical properties of Mg-Gd-Y-Zn-Zr alloy