DC Breakdown Strength of Crosslinked Polyethylene Based Nanocomposites at Different Temperatures

Shihang Wang,Shihu Yu,Jiao Xiang,Jianying Li,Shengtao Li

DOI: https://doi.org/10.1109/tdei.2019.008572

IF: 2.509

2020-01-01

IEEE Transactions on Dielectrics and Electrical Insulation

Abstract:Polyethylene based nanocomposites have been widely researched for being potential insulating materials in high voltage DC equipment. One of their key properties is the enhanced DC breakdown strength (Eb-DC). For a long time, the Eb-DC of polyethylene nanocomposites has been attributed to the deep charge traps located at the interphase region between the nanofiller and polymer matrix. In this work, we prepared XLPE/Al(OH)3 nanocomposites with 0.1 to 3 wt% nano-Al(OH)3 and studied their Eb-DC at 20 to 90 °C. The results show that the XLPE/Al(OH)3 nanocomposites possess significantly increased Eb-DC, although having a large amount of shallow charge traps, and more likely causing homocharge injection. The results of breakdown tests show that Eb-DC first increases and then decreases at 20 to 70 °C with increasing nanofiller while it shows a totally opposite trend at 90 °C. Eb-DC decreases dramatically with increasing temperature, a crossover phenomenon of Eb-DC appears at about 80 °C. The elastic modulus of XLPE/Al(OH)3 at different temperatures was obtained and it shows a similar trend with Eb-DC. Therefore, the mechanical properties influenced by morphology and space charge properties modulated by charge trap characteristics were analyzed to jointly determine the Eb-DC of XLPE/Al(OH)3 nanocomposites at different temperatures.