Abstract:The transition from polymeric alloy to a micropinned structure of XLPE‐PS leads to the development of deeper trapping sites with higher density. As a result, key electrical improvements, such as a remarkable enhancement in DC breakdown strength and a significant reduction in DC conductivity across electric field intervals, are achieved. This advancement leads to the development of reliable composite insulation. This research investigates the transition from a micropinned to a polymeric alloy structure in crosslinked‐polyethylene‐polystyrene (XLPE‐PS). Incorporating 2 wt% 10 μm PS particles into low‐density polyethylene (LDPE) and crosslinking with 2 wt% dicumyl peroxide (DCP) forms XLPE‐PS structures. The polymeric alloy structure, formed at 220°C extrusion, contrasts with the micropinned formed at 150°C. Morphological, thermo‐structural, chemical, and crystal properties are examined to understand their impact on electrical properties and charge transport mechanisms. Results indicate that the polymeric alloy effectively resolves void/crack issues, whereas the micropinned exhibits phase separation. Both structures exhibit a benzene‐crosslinked network, and variations in these structures lead to significant changes in thermo‐structural, chemical, and crystalline properties. The polymeric alloy XLPE‐PS shifts the polyethylene (PE) hkl crystal planes, confirming phase shift and optimal alloying. The structural alterations reveal deeper traps and higher densities in the polymeric alloy XLPE‐PS, leading to significantly improved electrical properties, including reduced DC conductivity by up to 1.3 and 0.7 decades at 30 and 90°C, and increased DC breakdown strength by up to 40.34% and 16.17% at 30 and 90°C, respectively, compared with micropinned XLPE‐PS. This research offers insights into stable high‐voltage insulation development.

Crosslinking Dependence of Direct Current Breakdown Performance for XLPE-PS Composites at Different Temperatures

Research on DC Breakdown Characteristics for the Insulation of 10 Kv AC XLPE Cables

DC Insulation Properties of Commercial Grade 320 Kv HVDC XLPE/MgO Nanocomposite Material

Electrical Insulation Performance of Cross‐linked Polyethylene/mgo Nanocomposite Material for ±320 Kv High‐voltage Direct‐current Cables

Crosslinking dependence of trap distribution and breakdown performance of crosslinked polyethylene

DC Breakdown Characteristics of LLDPE-based XLPE with Different Crosslinking Degrees

Electrical and Physico-chemical Properties of XLPE under Different Vulcanization Pressures for 500 Kv EHVDC Cable Factory Joint

Breakdown Characteristics and Electrical Life Evaluation of 500 Kv EHVAC Cable Insulation at Different Temperatures

Insights on the Breakdown Characteristics of PPLP under Different Test Protocols and Temperatures

Temperature Stability of DC Conductivity and Breakdown of Crosslinked LLDPE

DC Breakdown Strength of Crosslinked Polyethylene Based Nanocomposites at Different Temperatures

Temperature Dependence of Crystalline Structure and DC Performance in LLDPE/HDPE Blending Material

Effect of Blend of Polystyrene on the Temperature Dependence of DC Breakdown Characteristics of Polyethylene

Enhanced High-Temperature Dc Dielectric Performance Of Crosslinked Polyethylene With A Polystyrene Pinning Structure

Crosslinking-modulated direct-current conductivity of XLPE-PS composite via charge trap characteristics

Enhanced DC Breakdown Strength of XLPE Via Denser Cross-Linking Network Formation with Liquid Polybutadiene

Evolution from micropinned to polymeric alloy structure of XLPE‐PS: Improving electrical properties and mechanism

The Impact of Crosslinking Degree on DC Conductivity of LLDPE Based Insulation Materials

Temperature dependence of AC / DC breakdown strength of HVDC XLPE cable slices

Effects of Pre-Crosslinking on Space Charge and Breakdown Characteristics of XLPE Cable Insulation

Influence of Dicumy1 Peroxide Content on DC Performance of Polyethylene for DC Cables