DC Insulation Properties of Commercial Grade 320 Kv HVDC XLPE/MgO Nanocomposite Material

Ashish Paramane,Dai Chao,Linwei Yu,Xiangrong Chen,Yasuhiro Tanaka

2020-01-01

Abstract:The cross-linked polyethylene (XLPE) nanocomposite insulations exhibit the improved electrical properties for the high voltage cable application. This paper compares the DC insulation properties of as-received 320 kV HVDC XLPE/MgO nanocomposite material with the reference to pure XLPE at 25 °C test temperature. The MgO nanofiller dispersion is analyzed by scanning electron microscopy (SEM). DC breakdown strength is measured by applying the ramp voltage at a rate of 0.5 kV/s and space charge is measured at 50 kV/mm using the pulse electroacoustic system. Moreover, the test samples are exposed to the thermal aging at 135 °C for 30 days inside the hot-air oven. The fresh XLPE nanocomposite samples exhibit 20% higher DC breakdown strength and negligible hetero charge accumulation near the anode than fresh pure XLPE. The aforementioned properties of XLPE nanocomposite remain largely unaffected as compared to pure XLPE after its thermal aging. The thermal aging of pure XLPE decreases its DC breakdown strength by 38%, whereas the XLPE nanocomposite shows a 20% decrease. The thermal aging generates negligible hetero charges near the anode. However, significant hetero charges are accumulated near both electrodes after thermal aging inside the pure XLPE. The enhanced performance of the XLPE nanocomposite against thermal aging properties is attributed to its intact morphology.