Improved Plating Adhesion of Polyarylate Fibers via Supercritical CO2 and Impregnation of Slightly Soluble Oil on the Fiber Surface

Tomoki Sakai,Isao Tabata,Teruo Hori,Kazumasa Hirogaki

DOI: https://doi.org/10.1007/s12221-024-00532-5

IF: 2.5

2024-04-11

Fibers and Polymers

Abstract:There is a growing demand for conductive fibers with high bending resistance, particularly for applications, such as smart textiles and robot arms. The amount of fiber for such applications can be reduced using high-performance fibers with high tensile properties, such as polyaramid and polyarylate Vectran®). However, because such fibers are crystalline with rigid molecular structures, they poorly adhere to plated films; thus, the plated fibers exhibit poor bending fatigue resistance. To solve this problem, in this study, we expanded polyarylate fiber using supercritical CO 2 (ScCO 2 ) and impregnated it with a metal complex (palladium acetate), which acts as a catalyst for electroless plating to induce an anchoring effect. However, because polyarylate fiber has an extremely low polarity, it is difficult to uniformly impregnate it with many metal complexes, even with ScCO 2 . Generally, an organic solvent is added to tune the polarity of supercritical CO 2 ; however, the metal complex penetrates the fiber, thereby reducing the amount of metal complex near the fiber surface. Therefore, we tuned the polarity of the surface by applying various oils to the fiber surface. The sample electroplated in ScCO 2 with oil applied to its surface showed the highest bending fatigue resistance, followed by that treated in ScCO 2 without oil, and the sample treated in an aqueous solution showed the lowest. Furthermore, we measured the interfacial adhesion strength of the samples using the microdroplet method, and the same trend was observed.

materials science, textiles,polymer science

What problem does this paper attempt to address?

The paper mainly discusses how to improve the adhesion of the coating on polyarylate fibers (such as Vectran®) to enhance their bending durability in applications such as smart textiles and robotic arms. Due to the rigid crystalline structure of these high-performance fibers, their adhesion to the coating is poor, resulting in poor bending fatigue performance of the coated fibers.

Researchers improved the adhesion by using supercritical carbon dioxide (ScCO2) to expand the fibers and impregnating them with a metal complex (palladium acetate) as a catalyst for chemical plating, resulting in an anchoring effect. However, due to the extremely low polarity of polyarylate fibers, it is difficult to evenly impregnate the metal complex using ScCO2 alone. Usually, organic solvents need to be added to adjust the polarity of ScCO2, but this can cause the metal complex to penetrate into the fibers, reducing the amount of metal complex on the fiber surface.

To address this issue, the researchers found that the polarity of the fiber surface can be adjusted by applying oil that is slightly soluble in ScCO2, which increases the concentration of the catalyst on the fiber surface and improves the adhesion between the fiber and the metal coating. Experimental results showed that fibers treated with ScCO2 and oil had the highest bending fatigue resistance after electroplating, while water-based treated fibers exhibited the lowest performance.

The paper also describes the materials and methods, including the impregnation and reduction conditions of the fiber with palladium, electroplating process, resistance measurement, delamination test of the coating film, and analysis of the impact of different oils. Through these experiments, the researchers confirmed that fibers treated with ScCO2 and specific oils exhibited better mechanical properties and conductivity after electroplating.