Study on gear contact fatigue failure competition mechanism considering tooth wear evolution

Heli Liu,Huaiju Liu,Caichao Zhu,Jinyuan Tang
DOI: https://doi.org/10.1016/j.triboint.2020.106277
IF: 5.62
2020-01-01
Tribology International
Abstract:Contact fatigue issues are becoming more prominent in current gear anti-fatigue designs. Surface wear may result in unavoidable occurrence competition among contact fatigue failure modes such as micropitting and pitting. This work proposed a model incorporating the interface characteristics, mechanical properties and residual stress gradients to explore this competition mechanism during wear process of a wind turbine gear pair. Results reveal that the critical damage position moves deeper from near-surface to subsurface during the wear process, indicating that the most likely failure mode changes gradually from surface initiated contact failure to subsurface initiated contact failure. This illustrates that one-sided gear anti-fatigue designs may not satisfy the complex contact conditions because the dominant failure mode may change during operation.
What problem does this paper attempt to address?