Spalling Resistance of Thermally Grown Oxide Based on NiCoCrAlY(Ti) with Different Oxide Peg Sizes

Yang Liang,Choi Ryutan,Zheng Yu,Bidabadi Mohammad Hassan Shirani,Rehman Abdul,Zhang Chi,Chen Hao,Yang Zhi-Gang

DOI: https://doi.org/10.1007/s12598-019-01339-7

2020-01-01

Abstract:NiCoCrAlY is usually used as the material to bond-coat in thermal barrier coating systems under high temperatures. Using NiCoCrAlY and adding different amounts of the active element Ti (0, 0.1, 0.3, and 0.5; wt%), the relationship between oxide peg size and thermally grown oxide spalling resistance is ascertained by examining specimens subjected to a cyclic oxidation experiment. Oxide pegs, consisting of a Y- and Ti-rich oxide core and an outer Al 2 O 3 sheath, are formed by Ti and Al successively reacting with oxygen after the rapid generation of Y-rich oxide. The size of the oxide pegs with higher Ti concentrations is on average bigger in the alloy. Severe thermally grown oxide spalling occurred in the 0.5 wt% Ti specimen, but in the 0.3 wt% Ti specimen, it displayed the best adherence with the alloy due to the presence of fine pegs. Cavities existed at the interface between the inner oxide core and outer Al 2 O 3 sheath of larger pegs serve as microcrack sources and further induce severe scale failure combined with the initial interface crack between the scale and alloy.