Numerical analysis of interlaminar stress on symmetric angle-ply laminates interleaved with cnt networks
Lulu Shen,Wei Wang,Ling Liu
2017-01-01
Abstract:Delamination is one of the major initial damage forms for laminated composite structures, which is caused by relatively high interlaminar stress. In present study, glass fiber (GF)/epoxy (EP) symmetric angle-ply laminates, interleaved with carbon nanotube (CNT) networks at θ/-θ interfaces (10θ30), were used to analyses and evaluate the effect of CNT networks on interlaminar stress. This was realized by using of finite element analysis (FEA), based on cohesive zone model (CZM). Interlamiar stress distribution at +θ/–θ interfaces (CZM region) with and without CNT networks was calculated and compared. Numerical results show that the introduction of CNT networks into the interlaminar region improves the major interlaminar stress, which controls initiation and propagation of delamination. 1.INTRODUCTION Delamination beneath the surface of composite laminates will significantly degrade their mechanical properties and integrity, thus leading to abrupt structural failure. Delamination can be easily initiated by mode I and mode II loading [1-5], cyclic loading [6], impact [7]. It has also been shown that mode III-dominated delamination was tended to appear in symmetric angle-ply laminates due to the mismatch of mechanical properties in adjacent layers [8]. Therefore, delamination prediction is essential to the safe design for laminated composite structures. To date, intensive experimental and numerical investigations have already been conducted to obtain delamination data. In terms of experimental investigations, non-destructive testing (NDT), like acoustic emission (AE) [9-11], is one of the mature experimental methods to detect delamination in composite laminates. However, external sensors like AE strongly depend on the experience of manipulating personnel and sometimes are not convenient for practical application. In view of this, embedded sensors [12-14] have been developed to monitor delamination damage in real-time mode, whereas these sensors generally have limitations in detecting orientation and cause a reduction of in-plane mechanical properties. Recently, a newly emerging CNT based nano-detectors could break through the mentioned restrictions to real-time detect delamination, especially the CNT networks based nano-detectors [15-17]. Because of the isotropic property in plane, the CNT networks based nano-detectors are capable of detecting whole interlaminar region. Meanwhile, the excellent mechanical properties and extraordinary electrical ability of CNT make it potential to detect delamination damage in target area without hurting the overall mechanical properties of the composite laminates. On the other hand, it is worth noting that numerical simulation is an efficient and low-cost method to aid in understanding the complex mechanical behaviours and predicting damage process in composite structures. With the rapid development of computer technology, FEA has been extensively 21 International Conference on Composite Materials Xi’an, 20-25 August 2017 conducted to numerically investigate delamination. Since Virtual Crack Closure Technique (VCCT) has been proposed by Rybicki and Kanninen [18], it was available for calculating energy release rate of the delamination propagation [19-20]. The biggest weakness of VCCT is that it could only be used for predicting crack propagation rather than crack initiation. Extended finite element method (XFEM) is another common FEA approach [21-22], which was first put forward in 1999 by Belytschko and Black [23] to model delamination through simulating the opening or evolution of the crack. The introduced crack through XFEM is independent of the mesh, which constitutes a great advantage from the computational perspective. Besides, the crack’s propagation path could be observed. However, XFEM is only applicable in the vicinity of the crack and this method is failed to simulate the multiple crack growth. From the above-mentioned limitations, this paper adopts CZM, first introduced by Dugdale [24] and Barenblatt [25], as a finite element (FE) model to simulate delamination process by using ABAQUS commercial software. The cohesive layers can be located where delamination tended to occur with no need for specifying an initial defect or a pre-crack. Most researchers utilized CZM to simulate mode I and/or mode II delamination initiation and propagation in laminated composites [1-5], while lack of comprehensive studies investigated the aforementioned mode III-dominated delamination. This study focuses on the mode III-dominated delamination occurred in GF/ EP symmetric angle-ply laminates, interleaved with CNT networks at θ/-θ interfaces (10θ30), to investigate and compare the delamination behavior of the composite laminates with and without CNT networks. 2.CHARACTERIZING THE LAMINATES The constitutive properties of the composite materials were characterized by means of experiment tests and analytical method. The notations are reported in Figure 1, where 1, 2 and 3 refer to the fiber direction, transversal direction and thickness (normal) direction respectively. Mode I and mode II critical strain energy release rate (GIC, GIIC) were obtained through DCB and ENF tests in accordance with ASTM D5528 standard for the specimens with and without CNT networks. And mode III critical strain energy release rate (GIIIC) can be considered to be equal to GIIC in general. Moreover, according to ASTM D3039 and ASTM D5379, uniaxial tensile tests and Iosipescu (V-notched) shear tests were performed respectively to obtain the in-plane (intralayer) mechanical performances, i.e. E1, E2, ν12, and G12. Figure 1: Notations in unidirectional composite laminates. Conveniently, out-of-plane (interlaminar) mechanical properties are obtained through micro-mechanical law of composite materials. Out-of-plane shear modulus G23 is deduced from the assumption of transverse isotropy: