Abstract:In southern power grid, four 500kV composite wall bushings used at a converter station was found significantly aging after 15 years' operation, such as chalking, cracks and low hydrophobicity. The housing material of these wall bushings is liquid silicone rubber (LSR). In order to extend the service life, the out door insulation was repaired by RTV. As the internal failure, one of the four bushings was forced to be out of service. In this paper, the outer shed of the wall bushing was used to evaluate the aging characteristics of the LSR sheds after long term operation. The macroscopic aging characteristics of LSR sheds were investigated by using hydrophobicity and hydrophobicity transfer test, tensile and tear strength test. The microscopic characteristics of the aging sheds were obtained by using Scanning Electron Microsope (SEM), Fourier Transform Infrared Spectroscopy (FTIR) and X-ray Photoelectron Spectroscopy (XPS). It was found that the aging of the LSR shed developed from outer surface into the inside, and the layer structure including the chalking layer and the inner layer was obviously observed. The hydrophobicity, hydrophobicity transfer, tensile strength and tear strength of the aging sheds had different decrease. At microcosmic angle of view, the aging sheds appeared irregular shaped patches with a reduced surface roughness and adhesion; FTIR and XPS results indicated that the side chain groups of PDMS in the chalking layer were oxidized, crosslinked with other polysiloxane chains, forming more Si-O-Si groups, accompanied by the precipitation of TiO2 and white carbon black fillers. Due to the change of silicone rubber material from organic to inorganic, the content of C and Si elements in the chalking layer decreased, and the content of O element increased.The research also shows that, the hydrophobicity and hydrophobicity transfer of the aging LSR sheds can be improved by RTV repairment, but the appearance and hydrophobic changes still needs to be regularly monitored in the operation.

Simulation of the Chalking of Silicone Rubber Based on Tetramethylammonium-Hydroxide-Catalyzed Scission Reaction

Research on Controllable Artificial Chalking Method for Silicone Rubber

Study on the Chalking Mechanism of Silicone Rubber Composite Insulators

Identification and Characterization of the Chalking Layer of High Temperature Vulcanized Silicone Rubber

Enhanced Compatibility and Thermo-Oxidative Stability of Silicone Rubber/Ethylene–Propylene Terpolymer Composites Via in Situ Interface Coupling

Quantitative Approaches to Evaluating the Chalking Layer on Silicone Rubber

Effect Of Surface Modification Of Titanium Dioxide On The Uv-C Aging Behavior Of Silicone Rubber

Experimental Study and Mechanism Analysis of Composite Insulator Chalking in Extra-High Voltage (EHV) Transmission Line

The Influence of Water Permeation on the Chalking of HTV Silicone Rubber Composites

Aging Characteristics and Repairing Evaluation of Long-term Operating LSR Bushings

Hygrothermal ageing performance of high temperature vulcanised silicone rubber and its degradation mechanism

Effects of Silicone Rubber on Rheological Properties and Aging Characteristics of Asphalt Binder

Micro characterization and degradation mechanism of liquid silicone rubber used for external insulation

Preparation of chitosan‐based macromolecular synergistic antioxidants containing hindered phenolic and secondary amine structures and its effects on thermo‐oxidative aging of styrene‐butadiene rubber/silica composites

Catalytic upcycling of silicone rubber by AlCl 3 at low temperature

Efficiently Enhancing Low-dielectric Properties and Chemical Resistances of Addition-cure Liquid Silicone Rubber by Filling With Silicone-modified Eucommia Gum Nanofiller

Effect of Alumina Tri-Hydrate Surface Modification on Liquid Permeation and Electrical Performance of Silicone Rubber

Molecular dynamics supported thermal-moisture aging effects on properties of silicone rubber

Sulfur-Rich Ageing Mechanism of Silicone Encapsulant Used in LED Packaging: An Experimental and Molecular Dynamic Simulation Study

Fabrication of a novel chitosan‐based macromolecular antioxidant and its effects on the anti‐aging properties of styrene‐butadiene rubber/silica composites

Study on the influencing factors of natural degradation of liquid silicone rubber used for external insulation