Abstract:In southern power grid, four 500kV composite wall bushings used at a converter station was found significantly aging after 15 years' operation, such as chalking, cracks and low hydrophobicity. The housing material of these wall bushings is liquid silicone rubber (LSR). In order to extend the service life, the out door insulation was repaired by RTV. As the internal failure, one of the four bushings was forced to be out of service. In this paper, the outer shed of the wall bushing was used to evaluate the aging characteristics of the LSR sheds after long term operation. The macroscopic aging characteristics of LSR sheds were investigated by using hydrophobicity and hydrophobicity transfer test, tensile and tear strength test. The microscopic characteristics of the aging sheds were obtained by using Scanning Electron Microsope (SEM), Fourier Transform Infrared Spectroscopy (FTIR) and X-ray Photoelectron Spectroscopy (XPS). It was found that the aging of the LSR shed developed from outer surface into the inside, and the layer structure including the chalking layer and the inner layer was obviously observed. The hydrophobicity, hydrophobicity transfer, tensile strength and tear strength of the aging sheds had different decrease. At microcosmic angle of view, the aging sheds appeared irregular shaped patches with a reduced surface roughness and adhesion; FTIR and XPS results indicated that the side chain groups of PDMS in the chalking layer were oxidized, crosslinked with other polysiloxane chains, forming more Si-O-Si groups, accompanied by the precipitation of TiO2 and white carbon black fillers. Due to the change of silicone rubber material from organic to inorganic, the content of C and Si elements in the chalking layer decreased, and the content of O element increased.The research also shows that, the hydrophobicity and hydrophobicity transfer of the aging LSR sheds can be improved by RTV repairment, but the appearance and hydrophobic changes still needs to be regularly monitored in the operation.

Research on Controllable Artificial Chalking Method for Silicone Rubber

Simulation of the Chalking of Silicone Rubber Based on Tetramethylammonium-Hydroxide-Catalyzed Scission Reaction

Study on the Chalking Mechanism of Silicone Rubber Composite Insulators

Quantitative Approaches to Evaluating the Chalking Layer on Silicone Rubber

Effect Of Surface Modification Of Titanium Dioxide On The Uv-C Aging Behavior Of Silicone Rubber

Effect Of Titanium Dioxide On The Uv-C Ageing Behavior Of Silicone Rubber

Identification and Characterization of the Chalking Layer of High Temperature Vulcanized Silicone Rubber

Hygrothermal ageing performance of high temperature vulcanised silicone rubber and its degradation mechanism

Study on Aging Evaluation Method of Silicone Rubber in Dongguan

The Influence of Water Permeation on the Chalking of HTV Silicone Rubber Composites

Experimental Study and Mechanism Analysis of Composite Insulator Chalking in Extra-High Voltage (EHV) Transmission Line

Effects of Silicone Rubber on Rheological Properties and Aging Characteristics of Asphalt Binder

Molecular dynamics supported thermal-moisture aging effects on properties of silicone rubber

Aging Characteristics and Repairing Evaluation of Long-term Operating LSR Bushings

Study on the influencing factors of natural degradation of liquid silicone rubber used for external insulation

Research Progress of Aging Properties of Silicone Rubber

Surface‐modified mesoporous silica nanorods for the highly aging resistance rubber through controlled release of antioxidant

Application of Infrared Spectroscopy in Research on Aging of Silicone Rubber in Harsh Environment

Micro characterization and degradation mechanism of liquid silicone rubber used for external insulation

Thermal aging properties of flame retardant silicone rubber based on melamine cyanurate

Effect Of Ultraviolet-A Radiation On Surface Structure, Thermal, And Mechanical And Electrical Properties Of Liquid Silicone Rubber