Abstract:An equiatomic CoCrFeMnNi high-entropy alloy, which crystallizes in the face-centered cubic (fcc) crystal structure, was produced by arc melting and drop casting. The drop-cast ingots were homogenized, cold rolled and recrystallized to obtain single-phase microstructures with three different grain sizes in the range 4–160μm. Quasi-static tensile tests at an engineering strain rate of 10−3s−1 were then performed at temperatures between 77 and 1073K. Yield strength, ultimate tensile strength and elongation to fracture all increased with decreasing temperature. During the initial stages of plasticity (up to ∼2% strain), deformation occurs by planar dislocation glide on the normal fcc slip system, {111}〈110〉, at all the temperatures and grain sizes investigated. Undissociated 1/2〈110〉 dislocations were observed, as were numerous stacking faults, which imply the dissociation of several of these dislocations into 1/6〈112〉 Shockley partials. At later stages (∼20% strain), nanoscale deformation twins were observed after interrupted tests at 77K, but not in specimens tested at room temperature, where plasticity occurred exclusively by the aforementioned dislocations which organized into cells. Deformation twinning, by continually introducing new interfaces and decreasing the mean free path of dislocations during tensile testing (“dynamic Hall–Petch”), produces a high degree of work hardening and a significant increase in the ultimate tensile strength. This increased work hardening prevents the early onset of necking instability and is a reason for the enhanced ductility observed at 77K. A second reason is that twinning can provide an additional deformation mode to accommodate plasticity. However, twinning cannot explain the increase in yield strength with decreasing temperature in our high-entropy alloy since it was not observed in the early stages of plastic deformation. Since strong temperature dependencies of yield strength are also seen in binary fcc solid solution alloys, it may be an inherent solute effect, which needs further study.

Differences in Texture Evolution from Low-Entropy to High-Entropy Face-Centered Cubic Alloys During Tension Test

Systematic investigation of the texture evolution of Cu-Ni alloys with different strains

Dislocation slips assisted grain rotation and specific texture evolution in a CoCrNi medium entropy alloy

Mechanical behaviors and texture evolution of CoCrFeNi high-entropy alloy under shear-tension deformation

Analysis of the Ni-5%at.W Alloy Substrate Texture Evolution at Different Strain Levels Using the EBSD Technique

Grain size dependent microstructure and texture evolution during dynamic deformation of nanocrystalline face-centered cubic materials

Microstructure and Texture of Heavily Cold-Rolled and Annealed Fcc Equiatomic Medium to High Entropy Alloys

Texture Evolution and Plastic Deformation Mechanism of Cold-Drawn Co-Cr-Ni-Mo Alloy

In-situ EBSD study of deformation behavior of nickel-based superalloys during uniaxial tensile tests

In-situ observations of static recrystallization and texture formation in a cold-rolled CoCrFeMnNi high entropy alloy

Microstructure and Texture Evolution of Particle-Containing Aa3104 Alloy Cold Rolled to Large Strains

Microstructure and Texture Evolutions of Aa1050 Aluminum Alloy Cold Rolled to High Strains

Microstructure and texture of heavily cold-rolled and annealed extremely low stacking fault energy Cr26Mn20Fe20Co20Ni14 high entropy alloy: Comparative insights

Texture evolution and mechanical anisotropy of biomedical hot-rolled Co-Cr-Mo alloy

Portevin-Le Chatelier Mechanism in Face-Centered-cubic Metallic Alloys from Low to High Entropy

Evolution of Microstructure and Crystallographic Texture in Severely Cold Rolled High Entropy Equiatomic CoCrFeMnNi Alloy During Annealing

The influences of temperature and microstructure on the tensile properties of a CoCrFeMnNi high-entropy alloy

Mechanism of Crystallographic Orientation and Texture Evolution of Ti60 Alloy during Plane Strain Compression

Microstructure evolution in Cu-2.13Fe-0.026P (wt%): The contribution of texture intensity to residual stress variation

Microstructure and texture evolution during annealing of equiatomic CoCrFeMnNi high-entropy alloy

Influence of deformation and annealing twinning on the microstructure and texture evolution of face-centered cubic high-entropy alloys