Abstract:The method of making parts through additive manufacturing (AM) is becoming more and more widespread due to the possibility of the direct manufacturing of components with complex geometries. However, the technology's capacity is limited by the appearance of micro-cracks/discontinuities during the layer-by-layer thermal process. The ultrasonic (US) method is often applied to detect and estimate the location and size of discontinuities in the metallic parts obtained by AM as well as to identify local deterioration in structures. The Ti6Al4V (Ti64) alloy prepared by AM needed to acquire a high-quality densification if remarkable mechanical properties were to be pursued. Ultrasonic instruments employ a different type of scanning for the studied samples, resulting in extremely detailed images comparable to X-rays. Automated non-destructive testing with special algorithms is widely used in the industry today. In general, this means that there is a trend towards automation and data sharing in various technological and production sectors, including the use of intelligent systems at the initial stage of production that can exclude defective construction materials, prevent the spread of defective products, and identify the causes of certain instances of damage. Placing the non-destructive testing on a completely new basis will create the possibility for a broader analysis of the primary data and thus will contribute to the improvement of both inspection reliability and consistency of the results. The paper aims to present the C-scan method, using ultrasonic images in amplitude or time-of-flight to emphasize discontinuities of Ti64 samples realized by laser powder-bed fusion (L-PBF) technology. The analysis of US maps offers the possibility of information correlation, mainly as to flaws in certain areas, as well as distribution of a specific flaw in the volume of the sample (flaws and pores). Final users can import C-scan results as ASCII files for further processing and comparison with other methods of analysis (e.g., non-linear elastic wave spectroscopy (NEWS), multi-frequency eddy current, and computer tomography), leading to specific results. The precision of the flight time measurement ensures the possibility of estimating the types of discontinuities, including volumetric ones, offering immediate results of the inspection. In situ monitoring allows the detection, characterization, and prediction of defects, which is suitable for robotics. Detailing the level of discontinuities at a certain location is extremely valuable for making maintenance and management decisions.

Detection of Internal Holes in Additive Manufactured Ti-6Al-4V Part Using Laser Ultrasonic Testing

High precision detection of artificial defects in additively manufactured Ti6Al4V alloy via laser ultrasonic testing

Inspection of the Internal Defects with Different Size in Ni and Ti Additive Manufactured Components Using Laser Ultrasonic Technology

Laser ultrasonic testing for near-surface defects inspection of 316L stainless steel fabricated by laser powder bed fusion

Using Laser Ultrasound to Detect Subsurface Defects in Metal Laser Powder Bed Fusion Components

Investigation of the Effect of Artificial Internal Defects on the Tensile Behavior of Laser Powder Bed Fusion 17–4 Stainless Steel Samples: Simultaneous Tensile Testing and X-Ray Computed Tomography

Complementary Methods for the Assessment of the Porosity of Laser Additive-Manufactured Titanium Alloy

Nondestructive Testing of Defects in Additive Manufacturing Titanium Alloy Components

Detectability by X-ray micro computed tomography of fatigue initiating void defects in laser powder-bed additively manufactured Ti-6Al-4V coupons

Detecting Near-Surface Sub-Millimeter Voids in Additively Manufactured Ti-5V-5Al-5Mo-3Cr Alloy Using a Transmit-Receive Eddy Current Probe

Defect detection in additively manufactured AlSi10Mg and Ti6Al4V samples using laser ultrasonics and phase shift migration

Real-Time Nondestructive Evaluation of Additive Manufacturing Using a Laser Vibrometer and Shock Tube

Measurement of Elastic Constants of Additive Manufactured Ti-6Al-4V by Non-contact Multi-mode Laser Ultrasonic System

Quality Control Using Ultrasonic Phased Array Inspection of Components Produced by Directed Energy Deposition in Ti6Al4V Alloy

Phased array ultrasonic testing of micro-flaws in additive manufactured titanium block

3H-Imipramine binding in the blood platelets of normal twins

Non-contact imaging of subsurface defects using a scanning laser source

Use of X-ray Computed Tomography for Assessing Defects in Ti Grade 5 Parts Produced by Laser Melting Deposition

A non-destructive resonant acoustic testing and defect classification of additively manufactured lattice structures

Thermal-porosity characterization data of additively manufactured Ti-6Al-4V thin-walled structure via laser engineered net shaping

Study on the Surface/subsurface Defects of Cylindrical Components Based on Laser Ultrasonic Technology