Abstract:The method of making parts through additive manufacturing (AM) is becoming more and more widespread due to the possibility of the direct manufacturing of components with complex geometries. However, the technology's capacity is limited by the appearance of micro-cracks/discontinuities during the layer-by-layer thermal process. The ultrasonic (US) method is often applied to detect and estimate the location and size of discontinuities in the metallic parts obtained by AM as well as to identify local deterioration in structures. The Ti6Al4V (Ti64) alloy prepared by AM needed to acquire a high-quality densification if remarkable mechanical properties were to be pursued. Ultrasonic instruments employ a different type of scanning for the studied samples, resulting in extremely detailed images comparable to X-rays. Automated non-destructive testing with special algorithms is widely used in the industry today. In general, this means that there is a trend towards automation and data sharing in various technological and production sectors, including the use of intelligent systems at the initial stage of production that can exclude defective construction materials, prevent the spread of defective products, and identify the causes of certain instances of damage. Placing the non-destructive testing on a completely new basis will create the possibility for a broader analysis of the primary data and thus will contribute to the improvement of both inspection reliability and consistency of the results. The paper aims to present the C-scan method, using ultrasonic images in amplitude or time-of-flight to emphasize discontinuities of Ti64 samples realized by laser powder-bed fusion (L-PBF) technology. The analysis of US maps offers the possibility of information correlation, mainly as to flaws in certain areas, as well as distribution of a specific flaw in the volume of the sample (flaws and pores). Final users can import C-scan results as ASCII files for further processing and comparison with other methods of analysis (e.g., non-linear elastic wave spectroscopy (NEWS), multi-frequency eddy current, and computer tomography), leading to specific results. The precision of the flight time measurement ensures the possibility of estimating the types of discontinuities, including volumetric ones, offering immediate results of the inspection. In situ monitoring allows the detection, characterization, and prediction of defects, which is suitable for robotics. Detailing the level of discontinuities at a certain location is extremely valuable for making maintenance and management decisions.

Laser ultrasonic testing for near-surface defects inspection of 316L stainless steel fabricated by laser powder bed fusion

High precision detection of artificial defects in additively manufactured Ti6Al4V alloy via laser ultrasonic testing

Investigation of the Effect of Artificial Internal Defects on the Tensile Behavior of Laser Powder Bed Fusion 17–4 Stainless Steel Samples: Simultaneous Tensile Testing and X-Ray Computed Tomography

Using Laser Ultrasound to Detect Subsurface Defects in Metal Laser Powder Bed Fusion Components

Influence of surface roughness on laser ultrasonic detection for laser powder bed fusion manufactured 316L stainless steel

Anisotropy Evaluation and Defect Detection on Laser Power Bed Fusion 316L Stainless Steel

Creep-fatigue Properties and Deformation Mechanism of 316L Steel Fabricated by Laser Powder Bed Fusion (PBF-LB/M)

Ultrasonic testing of thick and thin Inconel 625 alloys manufactured by laser powder bed fusion

Defects quantification of additively manufactured AISI 316L stainless steel parts via non-destructive analyses: Experiments and semi-FEM-analytical-based modeling

In-situ visual monitoring for multi-scale defects detection in laser powder bed fusion

Inspection of thick welded joints using laser-ultrasonic SAFT

Defect detection in additively manufactured AlSi10Mg and Ti6Al4V samples using laser ultrasonics and phase shift migration

Microstructure and Fatigue Behavior of Laser-Powder Bed Fusion Austenitic Stainless Steel

Development of instrumentation for eddy current in situ monitoring of laser powder bed fusion

Porosity Evaluation and Analysis for 316L Stainless Steel by Selective Laser Melting Using Laser Ultrasonic Technology

Study on the Surface/subsurface Defects of Cylindrical Components Based on Laser Ultrasonic Technology

Pore defects in Laser Powder Bed Fusion: Formation mechanism, control method, and perspectives

Review of In Situ Detection and Ex Situ Characterization of Porosity in Laser Powder Bed Fusion Metal Additive Manufacturing

Complementary Methods for the Assessment of the Porosity of Laser Additive-Manufactured Titanium Alloy

In-situ Monitoring and Defect Detection of Selective Laser Melting Process and Impact of Process Parameters on the Quality of Fabricated SS 316L

Weldability of 316L Parts Produced by Metal Additive Manufacturing