Abstract:SiCf/SiC composite materials had become a research hotspot in the fields of aerospace materials and nuclear materials in recent years. This materials have high strength, radiation resistance, high temperature resistance and oxidation resistance. However, SiC is a typical brittle material prone to being damaged due to stress concentration in some cases, leading to cracks and even component failure. Therefore, this study employed an accurate and efficient numerical simulation method, phase field cohesive zone method (PFCZM), to investigate the microscopic damage behavior of SiCf/SiC composite materials. This study aimed to illustrate the influence of the thickness of pyrolytic carbon (PyC) interface layer on the failure behavior of SiCf/SiC composite materials. Firstly, this study conducted relevant verification of PFCZM. Secondly, numerical simulations of crack initiation, crack propagation, and final damage were performed by establishing a representative volume element (RVE). Observing the simulation results, it was noted that at low strain, when PyC was thicker, the SiCf/SiC composite materials exhibited slight damage to both the SiC matrix and PyC interface. Conversely, when PyC was thinner, the SiCf/SiC composite materials displayed only slight damage to PyC interface. As the PyC thickness increases, the damage to PyC interface decreases, while the damage to SiC becomes more prominent. Simultaneously, a competitive relationship in the damage behavior of SiCf/SiC composite materials can be found after the SiC matrix has cracked: When PyC is thinner, the damage primarily manifests as interlayer delamination between the SiC matrix and the SiC fiber. Conversely, when PyC is thicker, it manifests in PyC failure. Finally, this study concluded that, in this investigation, a PyC interface layer with a thickness of 0.1 μm exhibited the most effective protective effect on SiCf/SiC composite material.

The Microstructure Evolution in a SiCf/SiC Composite under Triple Ion Beam Irradiation

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

Microstructure Evolution of the Interface in SiCf/TiC-Ti3SiC2 Composite under Sequential Xe-He-H Ion Irradiation and Annealing Process

Evolution of microstructure and mechanical properties of SiCf/SiC composites induced by He ions irradiation at various temperatures

Microstructure characteristics of C+ and He+ irradiated SiCf/SiC composites before and after annealing

Damage Production in Silicon Carbide by Dual Ion Beams Irradiation

Microstructural Evolution of Polymer Derived SiC Ceramics and SiC/SiC Composite under 1.8MeV Electron Irradiation

Structure and fracture behavior of ion-beam-modified SiC-Al2O3-ZrO2 ceramic composites

Irradiation damage in silicon carbide based on a multi-mode scanning probe microscope

Helium irradiation induced microstructural damages and mechanical response of Al2O3-ZrO2-SiC composites

Optical and structural properties of 6H–SiC irradiated by Si3+⧹He+ coimplantation

Service characteristic evolution of three‐dimensional four‐directional braided C/SiC ceramic matrix composites under space electron radiation erosion environment

Defects Evolution in N-Type 4H-Sic Induced by Electron Irradiation and Annealing

Characterization of microstructure and hardening of SiC ceramic brazed joint using TiZrCuNi filler irradiated by He ions

Investigation of flexural behavior and microstructure of Amosic-3 silicon carbide composites under neutron irradiation

Ti3SiC2 irradiation damage at electron beam energy levels of 120 keV and 200 keV

Investigation on crack propagation of SiCf/SiC composite via PF-CZM method

Optical and Structural Properties of 6h–sic Irradiated by Coimplantation

Investigation of the damage behavior in SiC without any additives irradiated with Si ions by GIXRD, Raman and TEM

Evolution of structures and internal stress of ZrC-SiC composite under He ion irradiation and post-annealing

Novel microstructures on the surfaces of single crystal silicon irradiated by intense pulsed ion beams