Combined effects of irradiation and hydrogen on the mechanical and corrosion performances of the ferrite in duplex phase steels
Baolong Jiang,Ningning Liang,Lining Xu,Lei Gao,Qunjia Peng,Zhijie Jiao,Yongqing Chen,Weiguo Li,Yang He,Luning Wang,Lijie Qiao
DOI: https://doi.org/10.1016/j.jnucmat.2022.154069
IF: 3.555
2022-12-15
Journal of Nuclear Materials
Abstract:Structural materials in nuclear reactor cores suffer from severe corrosion and weakened mechanical properties under the combined influences of hydrogen and irradiation. In this study, we studied the peak damaged region (PDR) in the ferrite phase of a duplex stainless steel post proton irradiation, which is featured with a relatively higher concentration of hydrogen and level of irradiation damages than that of the uniformly damaged region (UDR). It is found that the irradiation-induced hardening effect is more evident in UDR than in PDR, and the PDR exhibits a much larger drop of electron work function and worse corrosion resistance than the UDR. Moreover, the oxide film on the PDR shows a much lower electrical resistivity than that of the UDR. The degradation of mechanical performance and corrosion resistance is associated with the local enrichment of hydrogen and the formation of G-phase in the PDR under the unique combined influence of hydrogen and irradiation. This study sheds lights on the synergetic effects of hydrogen and irradiation on the degradation of steels in reactor cores.
materials science, multidisciplinary,nuclear science & technology