Abstract:The resistances of Cu-SSZ-13 to hydrothermal aging and alkali metal poisoning for selective catalytic reduction of NOx with NH3 (NH3-SCR) were studied and comprehensive investigations were performed to better understand the poisoning mechanisms of the Cu-SSZ-13 catalyst. The NH3-SCR performance was well maintained after 700 °C hydrothermal aging for 12 h. With the aging temperature increasing to 750 °C, small decrease in the catalytic activity over the low temperature (<250 °C) and high temperature (>475 °C) range was observed due to the loss of some isolated Cu2+ ions and surface acidity in the hydrothermal-treated catalyst, whilst the NO conversion could still maintain over 90% in a wide temperature range (250–475 °C). Alkali metal (K, Ca, Na and Mg) was impregnated on Cu-SSZ-13 by an incipient wetness impregnation method, respectively. The Cu-SSZ-13 catalyst clearly exhibited a high resistance to alkali metal poisoning in a certain amount (0.50 mmol/gcatal), with the surface area, isolated Cu2+ ions and zeolite acidity largely maintaining after the alkali metal impregnation. The NH3-SCR activity was greatly reduced with a high content of alkali metal (1.50 mmol/gcatal) introduction, the zeolite structures were seriously deteriorated and the transformation of isolated Cu2+ ions to CuO was observed for all poisoned catalysts. The poisoning effect of studied alkali metal on the NH3-SCR performance was shown as follows: Mg > Ca > Na > K. The impregnation with Mg and Ca may cause more severe damage to zeolite structures and have more influence on the distribution of Cu2+/Cu+ than K and Na in the same metal loading. Furthermore, Mg2+ with the smallest diameter could replace with more isolated Cu2+ ions in the exchange sites and lead to the formation of abundant extra-framework CuO cluster.

Irregular Influence of Alkali Metals on Cu-SAPO-34 Catalyst for Selective Catalytic Reduction of NOx with Ammonia.

Potassium Poisoning on Cu-Sapo-34 Catalyst for Selective Catalytic Reduction of Nox with Ammonia

Steam and Alkali Resistant Cu-SSZ-13 Catalyst for the Selective Catalytic Reduction of NOx in Diesel Exhaust

The influence of chemical poisoning, hydrothermal aging and their co-effects on Cu-SAPO-34 catalyst for NOx reduction by NH3-SCR

Poisoning Mechanism of Alkali Metal on Cu–Fe2O3 Catalyst for Selective Catalytic Reduction of NO with NH3

Durability of Cu/SAPO-34 Catalyst for NOx Reduction by Ammonia: Potassium and Sulfur Poisoning

Location and Nature of Cu Species in Cu/SAPO-34 for Selective Catalytic Reduction of NO with NH3

Inhibition of Cu-SSZ-13 for NH 3 Selective Catalytic Reduction by K/Na Poisoning

Regulation of Al distributions and Cu2+ locations in SSZ-13 zeolites for NH3-SCR of NO by different alkali metal cations

Effects of Na+ on Cu/SAPO-34 for ammonia selective catalytic reduction.

The influence of sodium on the catalytic properties, low-temperature hydrothermal stability, and sulfur resistance of Cu-SAPO-34 for NOx reduction by NH3-SCR

Alkali poisoning of Fe-Cu-ZSM-5 catalyst for the selective catalytic reduction of NO with NH3

The Different Poisoning Behaviors of Various Alkali Metal Containing Compounds on Scr Catalyst

Potassium deactivation of Cu-SSZ-13 catalyst for NH<sub>3</sub>-SCR: Evolution of salts, zeolite and copper species

Investigation of low-temperature hydrothermal stability of Cu-SAPO-34 for selective catalytic reduction of NOx with NH3

Effect of Cu loading on the performance and kinetics of Cu/SAPO-34 catalysts for selective catalytic reduction with NH3

Chemical Deactivation of Cu-SAPO-18 Deno(x) Catalyst Caused by Basic Inorganic Contaminants in Diesel Exhaust

Local Dynamics of Copper Active Sites in Zeolite Catalysts for Selective Catalytic Reduction of NOx with NH3

Improving the Low-Temperature Hydrothermal Stability of Cu-SAPO-34 by the Addition of Ag for Ammonia Selective Catalytic Reduction of NO X

Research on Mechanism of the SCR Catalyst Deactivation by Alkali Metal During Entrained-Flow Combustion

Selective Catalytic Reduction of NOx with Ammonia over Copper Ion Exchanged SAPO‐47 Zeolites in a Wide Temperature Range