A Novel Tungstate Li3Nd3W2O12 with Garnet Structure for Low-Temperature Cofired Ceramic Technology

Ying Tang,Mingyang Yu,Zhiwei Zhang,Junqi Chen,Huaicheng Xiang,Xianran Xing,Liang Fang

DOI: https://doi.org/10.1016/j.jeurceramsoc.2019.11.083

IF: 5.7

2020-01-01

Journal of the European Ceramic Society

Abstract:Microwave dielectrics sintered at low temperature are pursued for energy saving and cofiring with cost-effective metallic electrodes (e.g. Cu, Ag and Al). In this study, a novel tungstate low-firing microwave dielectric ceramic, Li3Nd3W2O12, which can realise co-firing with Ag electrode at 940 degrees C, was synthesised by the conventional solid-state reaction method. According to the X-ray diffraction and Rietveld refinement results, Li3Nd3W2O12 crystallised in the garnet structure with a space group of Ia (3) over bar d and W6+ cations fully occupying the octahedral coordinated site. The optimum microwave dielectric properties with permittivity of similar to 9.8, quality factor of similar to 36,800 GHz and temperature coefficient of resonant frequency of similar to -30 ppm/degrees C were obtained after sintered at 940 degrees C. A near-zero temperature coefficient of resonant frequency of +3.6 ppm/degrees C was achieved in 0.96Li3Nd3W2O12-0.04CaTiO(3) ceramics. These properties make tungstate Li3Nd3W2O12 a promising candidate for low-temperature co-fired ceramic technology.