Abstract:The failure of thermal barrier coatings (TBCs) during operation depends mainly on the thermal mismatch between the ceramic top coat (TC) and the metal bond coat (BC). The thermal mismatch at the interface is influenced by the dynamic changes in the composition and morphology of the thermally grown oxide (TGO) between TC and BC during thermal cycling. This work focuses on the establishment of a TGO dynamic growth model, which considers the changes in TGO composition and morphology for investigating the effect of dynamic growth of TGO on local mismatch stresses during thermal cycling. The results show that the sharp locations at the TGO/BC interface are more prone to high tensile stresses during thermal cycling due to the uneven growth behavior of TGO, leading to crack initiation. The valley region of the interface is in a state of compressive stress σxx during the early stages of thermal exposure. The peak region preferentially forms a concentration of tensile stress σyy. Once large-scale "layer" (Ni, Co)Al2O4-based spinel-like mixed oxides(MO) growth occurs in TGO, the stress σxx changes from compressive stress to tensile stress in the valley region, eventually forming high tensile stress (Max: +158 MPa). The maximum tensile stress σyy in the peak region is increased to 256 MPa, which is more than two times larger than the early period of thermal exposure. As a result, the dramatic changes in local stresses seriously affect the time and location of microcracks.

Effect of Residual Stress on the Spallation of the Thermally-Grown Oxide Formed on NiCoCrAlY Coating

TGO stress growth for Pt-modified aluminide bond coats during high temperature oxidation

Characterization and Understanding of Residual Stresses in a NiCoCrAlY Bond Coat for Thermal Barrier Coating Application

Effect of Al Content on the Lifetime of Thermally Grown Oxide Formed on Ni–Al Alloys after Isothermal Oxidation

Improved Oxide Spallation Resistance of Microcrystalline Ni-Cr-Al Coatings

High Temperature Stress and Its Influence on Surface Rumpling in NiCoCrAlY Bond Coat

Spalling Resistance of Thermally Grown Oxide Based on NiCoCrAlY(Ti) with Different Oxide Peg Sizes

Time-dependent Spalling Behavior of Thermally Grown Oxide Induced by Room Temperature Interfacial Deformation

Effect of Oxide Growth on the Stress Development in Double-Ceramic-layer Thermal Barrier Coatings

Superior oxidation and spallation resistant NiCoCrAlY bond coat via homogenizing the yttrium distribution

Oxidation Behaviors of the NiCrAlY Bond Coats in the Thermal Barrier Coatings under External Loads

Analysis on the Residual Stresses in Functionally Gradient ZrO_2/NiCoCrAlY Coatings

Effect of Thermal Cycling Evolution on Residual Stress of High Emissivity Coating on Ni-Based Superalloy Sheet

Effect of Thermal Growth Oxide Composition and Morphology on Local Stresses in Thermal Barrier Coatings

Effect of Internal Oxidation on the Interfacial Morphology and Residual Stress in Air Plasma Sprayed Thermal Barrier Coatings

The failure behavior of thermally grown oxide of the AlCoCrFeNi bond coating prepared by atmospheric plasma spray at 900–1000 °C

The effect of tensile stress on oxidation behavior of nickel-base single crystal superalloy

Effect of microstructure of a NiCoCrAlY coating fabricated by high-velocity air fuel on the isothermal oxidation

Spallation Behaviour of Alumina Scale Formed on FeCrAlY Alloy After Isothermal Oxidation

A study on the thermal cyclic behavior of NiCrAlY coatings via femtosecond laser remelting with high repetition rate

Effect of Tensile Load on High Temperature Oxidation of CoNiCrAlY Coating