Designing Sb2Te3 Heterophase Homostructure
Xiaozhe Wang,Hangming Zhang,Xudong Wang,Jiangjing Wang,En Ma,Wei Zhang
DOI: https://doi.org/10.1360/tb-2022-0027
2022-01-01
Abstract:Antimony sesquitelluride (Sb2Te3) is the most important hosting material for the development of high-performance phase-change memory and brain-like computing technology. This material has two crystalline phases, namely, the metastable cubic rock-salt structure with 1/6 atomic sites taken by randomly distributed vacancies, and the stable rhombohedral phase with layered structures and vacant gaps in hexagonal stacking. The former is an Anderson insulator (AI) and serves as the key ingredient for memory applications, while the latter is a prototypical topological insulator (TI). In this work, we propose a new heterophase homostructure concept for Sb2Te3, which in principle could utilize both the topologically protected surface state of the rhombohedral phase and the Anderson localization features of the cubic phase in the bulk interior to achieve ultralow-loss electron transport. To sustain the topological surface state, the edges of the device should be kept in rhombohedral phase with the thickness larger than similar to 4 nm. The bulk interior of the sample should be transformed into cubic phase with strong electron localization. According to our density functional theory (DFT) results, the layered atomic building blocks for the two phases are quite similar, though their stacking sequence and degree of structural disorder are different. Thanks to the similar structure and mass density of the two phases, lattice mismatch is not expected to be present at the interface of the heterophase homostructure, superior to heterostructures made of different materials. To lend support to this heterophase homostructure concept, we have prepared a similar to 500 nm thick rhombohedral Sb2Te3 thin film on a silicon substrate via molecular beam epitaxy (MBE) and made an attempt to induce the phase transition in its bulk interior. A cross-sectional specimen for transmission electron microscopy (TEM) experiments was prepared by a dual beam focused ion beam (FIB) system. The TEM specimen along the electron beam direction was similar to 80 nm. For standard TEM observation in short time, the damage brought by electron beam is very limited. However, when the electron beam was focused in an exposure area of similar to 120 nm or below inside an electron microscope with a fixed accelerating voltage of 200 keV, visible structural changes in the Sb2Te3 specimen were observed. A gradual structural transition from the stable rhombohedral phase to the metastable cubic phase was observed under extensive electron beam irradiation over 90 min. The in situ high-resolution TEM experiments revealed a clear vacancy disordering induced metastabilization process in the Sb2Te3 specimen, where Sb atoms from the atomic stacks diffused into the vacant gap layers in Sb2Te3 and eventually triggered a structural change from rhombohedral to cubic Sb2Te3. Our DFT calculations corroborated this picture, which showed a systematic increase in total energy as the vacant gap was gradually filled in rhombohedral Sb2Te3. The bonding environment of the Sb atoms in the gap for the two phases is entirely different. For the cubic phase, the Sb atoms in the gap are located as the center of octahedral structures with the bond angle of similar to 90 degrees, which is consistent with the Sb atoms in the original rhombohedral and cubic phase. In stark contrast, the Sb atoms in the gap layers of rhombohedral phase are in a distorted bonding environment with bond angles of both similar to 110 degrees and similar to 90 degrees, leading to a large energy penalty for the rhombohedral phase. When the concentration of vacancies in the target layers reached 50%-70%, a change in stacking sequence from rhombohedral to cubic stacking was triggered. The critical vacancy concentration was mainly affected by the degree of compressive strain perpendicular to the target layers. In summary, we have discussed the design concept of a Sb2Te3 based heterophase homostructure and demonstrated that this structure could be free of lattice mismatch via in situ TEM experiments and DFT calculations. Finally, we provided some guidelines for practical synthesis of Sb2Te3 heterophase homostructure samples to explore the interaction between topological physics and Anderson localization of electrons, and to fabricate potential electronic devices of ultra-low power consumption.