Abstract:The failure of fiber-reinforced ceramic and metal matrix composites under a fixed load for extended times occurs because of strength degradation in the constituent fibers. Specifically, the ceramic fibers possess a Weibull strength distribution caused by crack-like flaws, which can grow according to a power-law growth mechanism. Failure of individual fibers causes interfacial slippage and stress redistribution to unfailed fibers, which in turn accelerates the degradation rate of the remaining fibers, and culminates in abrupt failure of the composite after sufficient damage has accumulated. This sequence of events is modeled both analytically and numerically within the Global Load Sharing (GLS) approximation previously utilized for quasi-static loading. Analytically, a general constitutive model for the relationship between the stress on the damaged fiber bundle, the strain in the unbroken fibers, and the extent of damage, is combined with a time-dependent damage evolution equation derived from the slow-crack-growth kinetics to yield an integral equation for the strain vs time at fixed applied load. The relevant gauge length for a fixed-load rupture process is found to be δ = rστ which is twice the slip length prevailing at the initial applied load σ, where τ is the interfacial sliding resistance between fiber and matrix. The underlying time scale for rupture is the time scale for a typical fiber of gauge length δ to fail under the applied load σ; this time can be quite different from that measured by stress-rupture tests on single fibers at an unrelated laboratory gauge length L0. A simple, accurate but approximate relationship between applied load, time to failure, fiber Weibull modulus, and slow crack growth exponent is presented. The numerical simulations of the same degradation process verify the general accuracy of the failure time obtained from the analytic results. The remaining tensile strength after some time at load but prior to failure is also studied, and the simulation results generally exhibited a more sudden-death failure than the analytical predictions. A specific application to the failure of a Nicalon fiber composite is presented.

Influence of statistical fiber strength distribution on matrix cracking in fiber composites

The mechanics of matrix cracking in brittle-matrix fiber composites

Tensile properties of short fiber composites with fiber strength distribution

Steady-state and multiple cracking of short random fiber composites

Stochastic Aspects of Matrix Cracking in Brittle Matrix Composites

Stochastic Process of Multiple Cracking in Discontinuous Random Fiber Reinforced Brittle Matrix Composites

Multiple Cracking of Fiber/Matrix Composites - Analysis of Normal Extension

Analysis of Fiber Breaking in Fiber/matrix Composites under Torsional Loads

Matrix crack spacing in brittle matrix composites

Micromechanical analysis of stochastic fiber/matrix interface strength effect on transverse tensile property of fiber reinforced composites

Effect of Fiber Extensibility on the Fracture Toughness of Short Fiber or Brittle Matrix Composites

Matrix cracking of fiber-reinforced ceramic composites in shear

Effect of Multiple Matrix Cracking on Crack Bridging of Fiber Reinforced Engineered Cementitious Composite

Interactive Growth of Multiple Fiber-Bridged Matrix Cracks in Unidirectional Composites

Critical crack-length during fracture

Stochastic aspects of crack deflection and crack path prediction in short fiber reinforced polymer matrix composites

Time-dependent failure in fiber-reinforced composites by fiber degradation

Critical crack length during fracture

Analysis for a Broken and Debonging Fiber in Ductile Matrix Composites

Elastic-Plastic Fracture Behavior Analysis On A Griffith Crack In The Cylindrical Three-Phase Composites With Generalized Irwin Model

Fatigue accumulated damage in notched quasi-isotropic composites under high-temperature conditions: A discussion on the influence of matrix nature on the stress energy release rate