Abstract:Understanding of cracking opening behavior is important for the prediction of residual strength and lifetime of silicon carbide fiber-reinforced silicon carbide ceramic–matrix composites at elevated temperatures. Under tensile loading below the proportional limit stress, multiple matrix cracking modes in the longitudinal and transverse yarns of a two-dimensional plain-woven silicon carbide fiber-reinforced silicon carbide composite appear in the matrix with debonding at the fiber/matrix interface. Crack opening displacement is a key parameter to characterize the crack opening behavior in silicon carbide fiber-reinforced silicon carbide composites and is affected by the multiple matrix cracking modes. In this article, a damage-based micromechanical crack opening displacement model for two-dimensional plain-woven silicon carbide fiber-reinforced silicon carbide composites is developed considering different matrix cracking modes. Two typical matrix cracking modes in a two-dimensional plain-woven silicon carbide fiber-reinforced silicon carbide composite, that is, cracking mode III with cracking in the matrix of the longitudinal and transverse yarns and cracking mode V with cracking only in the matrix of the longitudinal yarns, are considered. Micro stress field in the fiber, matrix of the longitudinal yarns, and transverse yarns are obtained. The crack opening displacement and related damage parameters are determined. Relationships between composite's crack opening displacement, constitutive properties, woven parameters, and damage state are established. Experimental crack opening displacements of cracking modes III and V in a two-dimensional plain-woven melt-infiltration silicon carbide fiber-reinforced silicon carbide composite from the published literature are predicted. For cracking mode III with partial interface debonding, the crack opening displacement increased nonlinearly with applied stress; and for cracking mode V with complete interface debonding, the crack opening displacement increased linearly with applied stress.

Matrix crack spacing in brittle matrix composites

Stochastic Aspects of Matrix Cracking in Brittle Matrix Composites

The mechanics of matrix cracking in brittle-matrix fiber composites

Stochastic Process of Multiple Cracking in Discontinuous Random Fiber Reinforced Brittle Matrix Composites

Matrix cracking of fiber-reinforced ceramic composites in shear

Interactive Growth of Multiple Fiber-Bridged Matrix Cracks in Unidirectional Composites

Effect of Multiple Matrix Cracking on Crack Bridging of Fiber Reinforced Engineered Cementitious Composite

Influence of statistical fiber strength distribution on matrix cracking in fiber composites

Multiple Cracking of Fiber/Matrix Composites - Analysis of Normal Extension

Steady-state and multiple cracking of short random fiber composites

Elastic-Plastic Fracture Behavior Analysis On A Griffith Crack In The Cylindrical Three-Phase Composites With Generalized Irwin Model

A fibre direction informed continuum damage model with enriched kinematics for modelling matrix cracking in composites

Effect of Fiber Extensibility on the Fracture Toughness of Short Fiber or Brittle Matrix Composites

An approach to estimate crack opening displacement in two-dimensional plain-woven silicon carbide fiber-reinforced silicon carbide composite considering different matrix cracking modes

A Zener–Stroh Crack in Fiber-Reinforced Composites with Generalized Irwin Plastic Zone Correction

Growth behavior of short fatigue cracks in a unidirectional SiC fiber-reinforced titanium matrix composite under spectrum loading

Doubly periodic arrays of bridged cracks and short fibre-reinforced cementitious composites

A generic model to determine crack spacing of short and randomly oriented polymeric fiber-reinforced strain-hardening cementitious composites (SHCC)

The Effects of Matrix Cracks on the Nonlinear Vibration Characteristics of Shear Deformable Laminated Beams Containing Carbon Nanotube Reinforced Composite Layers

Critical crack length during fracture

Critical crack-length during fracture