Abstract:Adding nano particles were supposed to displace steaming curing in manufacturing prefabricated components of concrete for avoiding thermal damage. Nevertheless, there were not yet appropriate nano particles adapted for practical production, and the main reason was those existing nano particles involved complicated technological processes and high costs. Last incompatibility with cement-based materials confined to its application. In this study, a new early strength agent was prepared by wet-grinding concrete waste slurry (CWS). The physico-chemical properties of CWS after wet-grinding were analyzed by means of XRD, the particle size distribution (PSD), ICP, SEM, pH, resistivity, and TG. Finally, the effects of CWS on the early hydration processes and me-chanical properties of cement-based materials were explored by means of setting time, hydration heat, chemical shrinkage, resistivity, mechanical properties, and MIP. The results showed that the particle size of CWS after wet -grinding decreased (D50 = 0.7 mu m). Meanwhile, the surface area and the dissolution of alkaline ions in the solution increased, which provided nucleation sites and the alkaline environment for the early hydration of cement-based materials. Moreover, the early hydration rate of cement and mechanical properties were greatly improved. For instance, the cumulative heat release at 12 h increased by 111.7%, the induction period was shortened, the gel hole increased by 8% in 12 h, the large hole decreased by 37%, and the initial and final coagulation time was shortened by >30%, the compressive strength at 12 h increased by 406.3%, and the compressive strength was basically equivalent in the later period. The research in this paper showed that it was feasible to prepare the new early strength agent from CWS through the wet-grinding treatment, which provided a new reference for the green development of the prefabricated component industry.

New Treatment Technology: the Use of Wet-Milling Concrete Slurry Waste to Substitute Cement

A Comparative Study on Concrete Slurry Waste: Performance Optimization from the Wet-Milling Process

Eco-Friendly Treatment of Humid Hardened Concrete Waste and Its Reuse in Concrete

Effect of Wet Grinding Concrete Slurry Waste on Hydration and Hardening Properties of Cement: Micro-Nano-Scale Modification

Research on Sustainable Development of Fine-Grained Material Cement Slurry

Feasibility Analysis For Utilization Of Sewage Sludge Incineration Ash As Cement Replacement

Pre-treatment of Reclaimed Concrete Slurry Waste for Substituting Cementitious Materials: Effect of Treatment Approach and Substitution Content

Humid Hardened Concrete Waste Treated by Multiple Wet-Grinding and Its Reuse in Concrete

A Novel Early Strength Agent Prepared by Wet-Grinding Concrete Waste Slurry and Its Effect on Early Hydration and Mechanical Properties of Cement Based Materials

Influence of replacing Portland cement with three different concrete sludge wastes

Achieving Carbon Utilization and Storage (CUS) in Cement-Based Materials with Wet-Grinding Carbonated Concrete Slurry Waste

Research on Cement Slurry Using Silica Fume Instead of Fly Ash

Experimental Research on the Performance of Recycled Waste Concrete Powder (RWCP) on Concrete

Mechanical performance and environmental potential of concrete with engineering sediment waste for sustainable built environment

Studies on Mechanism of Activity of Fly Ash-Cement Slurry Improved by High-Energy Ball Milling

Recycling of water treatment sludge in concrete: The role of water-binder ratio from a nanoscale perspective

Research on strength and workability of concrete with slag slurry processed by wet-milling

Influence of industrial waste and mineral admixtures on durability and sustainability of high-performance concrete

Recycling hazardous water treatment sludge in cement -based construction materials: Mechanical properties, drying shrinkage, and nano-scale characteristics

Study on Early Shrinkage and Mechanical Properties of Concrete with Various Cementitious Materials

Recycling of Plastic Waste Concrete to Prepare an Effective Additive for Early Strength and Late Permeability Improvement of Cement Paste