Effect of Fe2O3 additive on microstructure and high temperature tensile properties of oxide dispersion-strengthened Fe12CrWTiY alloys
Wei GUO,Zu-ming LIU,Liu-jie ZHANG,Yong LIU,Li-qing HUANG,Xiao-feng LI
DOI: https://doi.org/10.3969/j.issn.1673-0224.2012.05.002
2012-01-01
Abstract:Oxide dispersion-strengthened(ODS) Fe-12Cr-2.5W-0.4Ti-0.25Y(mass fraction,%) alloys were fabricated by gas-atomized prealloy powders with 1% Fe2O3additive as the oxygen carrier.High temperature tensile properties,phase composition,microstructure and fracture morphology of the alloys with and without Fe2O3 additive were studied.Experimental results show that the addition of Fe2O3refines the average grain size of the prepared alloys from 8.6 μm to 7.3 μm.In addition to the nanoscale Ti2Y2O7second phase,there also exist several other kinds of complex oxide particles in the matrixes,including Y3Fe5O12,Cr1.3Fe0.7O3 and(Cr0.88Ti0.12)2O3 with sizes of 20~200 nm and 1~10 μm,along with lath-like structures with width of 200~300 nm and 5~30 nm.The tensile strength of the alloy was estimated to be 1257,1108 and 128 MPa at room temperature,550 and 850 ℃,respectively,increased by 50.7%,39% and 30.6% compared with the alloy without Fe2O3 additive.Addition of Fe2O3 can improve the dispersion strengthening effect by increasing the number of dispersive oxides in the alloys.However,upon high temperature,micro-scale oxide particles were observed to separate from the alloy matrix probably owing to their different expansion coefficients,leading to preferential crack formation and thus deteriorated high-temperature tensile properties.