Feasibility of using Y 2 Ti 2 O 7 nanoparticles to fabricate high strength oxide dispersion strengthened Fe–Cr–Al steels

tong liu,linbo wang,chenxi wang,hailong shen,hongtao zhang
DOI: https://doi.org/10.1016/j.matdes.2015.08.118
IF: 9.417
2015-01-01
Materials & Design
Abstract:Addition of Al can improve the corrosion resistance of oxide dispersion strengthened (ODS) steels. However, Al reacts with Y2O3 to form large Y–Al–O particles in the steels and deteriorates their mechanical properties. Herein, we successfully prepared Y2Ti2O7 nanoparticles (NPs) by the combination of hydrogen plasma-metal reaction (HPMR) and annealing. Y2Ti2O7 NPs with contents of 0.2 or 0.6wt.% were then added into the Fe–14Cr–3Al–2W–0.35Ti (wt.%) steel to substitute the conventional Y2O3 NPs by mechanical alloying (MA). The Y2Ti2O7 NPs transformed into amorphous-like structure after 96h MA. They crystallized with a fine size of 7.4±3.7nm and shared a semi-coherent interface with the matrix after hot isostatic pressing (HIP) of the ODS steel with 0.6wt.% Y2Ti2O7. With the increasing Y2Ti2O7 content from 0.2 to 0.6wt.%, the tensile strength of the ODS steel increased from 1238 to 1296MPa, which was much higher than that (949MPa) of the ODS steel added with Y2O3. The remarkably improved mechanical properties of the Al-containing ODS steels were attributed to the increasing number density of Y2Ti2O7 nanoprecipitates. Our work demonstrates a novel route to fabricate high performance ODS steels with both high mechanical strength and good corrosion resistance.
What problem does this paper attempt to address?