Abstract:Defect-free SLM-IN 738LC superalloy samples were fabricated using selective laser melting (SLM). The as-built samples exhibit a cellular structure with fine carbides, γ′ phases, and high-density dislocations at the cell boundary and nano-size γ′ phases in the interior, resulting in excellent deformation resistance and favorable mechanical properties at room temperature, with a yield strength (YS) of 970 MPa, an ultimate tensile strength (UTS) of 1263 MPa, and an elongation (EL) of 33%. This study investigates the evolution behavior of the γ′ phase at different solid solution treatment (SHT) temperatures and its impact on alloy strength and toughness. The 1020 + AHT sample exhibits a uniform distribution of coarse γ′ phases. The samples subjected to 1070 + AHT and 1120 + AHT display a bimodal distribution of γ′ phases. When the SHT temperature was further increased, fine spherical γ′ phases are evenly distributed in the 1160 + AHT and 1200 + AHT samples. Moreover, the γ/γ′ eutectics at the grain boundaries gradually dissolve with increasing SHT temperature, whereas the size and fraction of carbides increase. The room temperature tensile test of the 1070 + AHT sample demonstrated a favorable balance between strength and plasticity (YS = 1217 MPa, UTS = 1472 MPa, EL = 9.25%). This is attributed to the synergistic strengthening effect of the bimodal distribution of the γ′ phase. The temperature-dependent deformation behavior of the 1070 + AHT sample was analyzed at 23 °C, 800 °C, 900 °C, and 1000 °C. At 23 °C, numerous dislocations accumulated around the γ/γ′ interfaces. When the temperature increased to 800–900 °C, the dislocations shearing γ′ phases is activated and the alloy remained high strength. At 1000 °C, both the dislocation shearing and dislocation bypassing mechanisms coexist, resulting in a decrease in the strength of the alloy and an increase in its plasticity. This work provides scientific and theoretical support for SLM-IN 738LC parts with favorable properties.

Selective laser melting of the hard-to-weld IN738LC superalloy: Efforts to mitigate defects and the resultant microstructural and mechanical properties

In-situ Study of Microstructure and Mechanical Properties of GH3536 Alloy Manufactured by Selective Laser Melting at 750 °C

Selective laser melting of IN738 superalloy with a low Mn+Si content: Effect of energy input on characteristics of molten pool, metallurgical defects, microstructures and mechanical properties

Enhanced Mechanical Properties of the Additively Manufactured IN738LC Superalloy Through Thermal History Management During the Laser Powder Bed Fusion Process

Microstructure, mechanical properties and strengthening mechanisms of IN738LC alloy produced by Electron Beam Selective Melting

Influence of Scanning Strategy and Post-Treatment on Cracks and Mechanical Properties of Selective-Laser-Melted K438 Superalloy

Microstructural Evolution and High-Temperature Strengthening Mechanisms of the in 738LC Superalloy Prepared by Selective Laser Melting

Microstructural Evolution and Defect Formation in a Powder Metallurgy Nickel-Based Superalloy Processed by Selective Laser Melting

Cracking Mechanism and Susceptibility of Laser Melting Deposited Inconel 738 Superalloy

Selective Laser Melting Enabled Additive Manufacturing of Ti-22Al-25Nb Intermetallic: Excellent Combination of Strength and Ductility, and Unique Microstructural Features Associated

Grain refinement and crack inhibition of hard-to-weld Inconel 738 alloy by altering the scanning strategy during selective laser melting

On the solidification behaviour and cracking origin of a nickel-based superalloy during selective laser melting

Investigation of Microstructure and Mechanical Performance of IN738LC Superalloy Thin Wall Produced by Pulsed Plasma Arc Additive Manufacturing

High temperature material properties of IN738LC processed by selective laser melting (SLM) technology

Selective Laser Melting of Non-Weldable Nickel Superalloy: Microstructure, Cracks and Texture

Microstructural Characteristics and Mechanical Properties of an Additively Manufactured Nickel-Based Superalloy

Selective laser melting additive manufacturing of 7xxx series Al-Zn-Mg-Cu alloy: Cracking elimination by co-incorporation of Si and TiB2

An Investigation of the Microstructural Evolution and Tensile Properties of a Nickel-Based GH648 Superalloy Manufactured Through Selective Laser Melting

Influence of Selective Laser Melting Process Parameters on Microstructure and Properties of a Typical Ni-Based Superalloy

Selective Laser Melting of Crack-Free René 104 Superalloy by Sc Microalloying

High-temperature mechanical properties of nickel-based superalloys manufactured by additive manufacturing