Abstract:IN738 superalloy with excellent high-temperature performance is of huge interest for hot-end component applications in aerospace, but its additive manufacturing via selective laser melting (SLM) is rather challenging due to the unsolved high crack susceptibility. Here, for the purpose of improving the formability of IN738 in SLM, Mn + Si content was then strictly controlled in raw powder. An orthogonal experiment was then carried out under different energy inputs to investigate the characteristics of the molten pool, metallurgical defects, microstructures, and mechanical properties of IN738 by SLM. The results showed that high laser power was more likely to shape large melting depth and depth-to-width ratio under the same linear energy density (LED), rather than scanning speed. Four morphologies of the molten pool were observed in the entire LED range. At lower LEDs, hot cracks were usually accompanied by irregular pores due to the stress concentration at the sharp corner of pores; at higher LEDs, cracks were located at the interface of grain boundaries with large misorientation angles. Energy dispersive spectrometry results revealed that the presence of Al-rich oxides and high Mn + Si content at the interface were the main reasons for cracking. The Scheil-Gulliver solidification modeling was used to examine the cracking susceptibility of Si and Mn elements. In addition, both dendrites and cellular dendrites were found in columnar grain structures. By reducing the Mn + Si content and optimizing process, crack-free and nearly fully dense samples of IN738 were obtained by SLM with excellent mechanical properties (ultimate tensile strengths = 1206 MPa, yield strength = 866 MPa and elongation = 16.5%), which were much higher than the mechanical properties of conventionally manufactured IN738.

Grain refinement and crack inhibition of hard-to-weld Inconel 738 alloy by altering the scanning strategy during selective laser melting

In-situ Study of Microstructure and Mechanical Properties of GH3536 Alloy Manufactured by Selective Laser Melting at 750 °C

Influence of Scanning Strategy and Post-Treatment on Cracks and Mechanical Properties of Selective-Laser-Melted K438 Superalloy

Selective laser melting of IN738 superalloy with a low Mn+Si content: Effect of energy input on characteristics of molten pool, metallurgical defects, microstructures and mechanical properties

A Novel Grain Refinement Design to Inhibit Liquation Cracking in Laser Cladding Non-Weldable Nickel-Based Alloy

A novel method to prevent cracking in directed energy deposition of Inconel 738 by in-situ doping Inconel 718

Tailored microstructure by using in-situ re-scanning and its influence on fatigue crack growth behavior of Inconel 718 fabricated by LPBF at elevated temperature

Cracking inhibition of nano-TiC reinforced René 104 superalloy fabricated by selective laser melting

Mechanical properties and microstructure evolution of selective laser melting Inconel 718 along building direction and sectional dimension

A new strategy to inhibit stray grain formation during laser directed solidification of single crystal superalloys

Additively manufactured crack-free nickel-based superalloys with synergistic strength and plasticity via grain refinement and striped oxides inhibition

Origin of hot cracking formation and suppression method in laser additive manufactured nickel-based superalloys

Crack Formation and Control in an AlCoCrFeNi High Entropy Alloy Fabricated by Selective Laser Melting

Effect of scanning strategies on microstructure and wear behavior of Inconel 718 fabricated by Selective Laser Melting

Grain boundary network evolution in electron-beam powder bed fusion nickel-based superalloy Inconel 738

Effect of Layer-Wise Varying Parameters on the Microstructure and Soundness of Selective Laser Melted INCONEL 718 Alloy

Selective laser melting additive manufacturing of 7xxx series Al-Zn-Mg-Cu alloy: Cracking elimination by co-incorporation of Si and TiB2

Effect of Scanning Angle on Grain Growth and Mechanical Properties of Ni10cr6w1fe9ti1 Hea

High-temperature mechanical properties of nickel-based superalloys manufactured by additive manufacturing

Grain refinement and mechanical properties improvement of Inconel 625 alloy fabricated by ultrasonic-assisted wire and arc additive manufacturing

Effects of Thermal Stress on the Formation and Cracking Behavior of Nickel-Based Superalloys by Selective Laser Melting Based on a Coupled Thermo-Mechanical Model