Seeding-free Synthesis of High-Performance MFI Zeolite Membranes on Superhydrophobic Supports Inspired by “like Grows Like” Principle

Xixi Ma,Xiaocao Wu,Juergen Caro,Aisheng Huang

DOI: https://doi.org/10.1016/j.micromeso.2019.109589

IF: 5.876

2019-01-01

Microporous and Mesoporous Materials

Abstract:A seeding-free synthesis strategy was developed for the preparation of dense and phase-pure MFI zeolite membranes based on "like grows like" principle. Through covalent modification of the porous ceramic supports by using 1H,1H,2H,2H-perfluoroalkyltriethoxysilanes (POTS), the support surface was changed from hydrophilic to hydrophobic, which promotes the nucleation and growth of hydrophobic MFI zeolite membranes. Thin, well-intergrown and phase-pure MFI zeolite membranes, with a thickness of about 2.0-3.0 mu m, can be facilely prepared on POTS-modified supports like Al2O3 and TiO2 at 175 degrees C for 24 h. No cracks, pinholes or other visible macroscopic defects are observed in the membrane layer. The MFI zeolite membranes were evaluated in the hydrophobic separation of 5.0 wt% ethanol/water mixture at 75 degrees C by pervaporation. The MFI zeolite membrane prepared on the POTS-modified TiO2 disk shows high pervaporation separation for ethanol recovery. At 75 degrees C, a separation factor of 103 and total flux of 2.56 kg/m(2)h can be obtained, which is promising to extract bio-alcohols from the fermentation broth.