Pure‐silica MFI zeolite membrane by cooperative templating approach for ethanol‐water separation

Jiancheng Lan,Linzhe Li,Wensen Song,Hammad Saulat,Haowen Wu,Jianhua Yang,Chengmin Yang,Yang Li,Jinming Lu,Yan Zhang

DOI: https://doi.org/10.1002/aic.17184

IF: 4.167

2021-01-23

AIChE Journal

Abstract:<p>Pure‐silica MFI zeolite membrane composed of intergrown four prism crystals was fabricated by using tetrabutylammonium (TBA⁺) and tetraethylammonium (TEA⁺) as cooperating templates and the induced function of MFI seeds under synthesis solution with molar composition of 1TEOS:0.2TBAOH:0.2TEABr:180H₂O. The ethanol/water separation factor was 64 with a flux of 1.40 kg m^‐2 h^‐1 for 5 wt. % ethanol/water mixture at 60 °C. In contrast, single TBAOH and TEAOH template led to formation of uncontinuous MEL and MFI membrane respectively, without ethanol‐selectivity. The behavior of quaternary ammonium (TBA⁺ and TEA⁺) varied in different system: 1) In "TBA⁺+ TEA⁺" system, TBA⁺ and TEA⁺ were incorporated into MFI zeolite channel simultaneously; 2) In "TPA⁺+ M⁺" system (M=TEA or TBA), either TEA⁺ or TBA⁺ couldn't be occluded into channel, however, appropriate amount of TBA⁺ could accelerate membrane crystallization, meanwhile increase in TEA⁺ slowed down crystallization rate of MFI membrane. This work extends the alternative preparation approaches of ethanol perm‐selective MFI membrane.</p><p>This article is protected by copyright. All rights reserved.</p>

engineering, chemical