Abstract:Cu1.8S-based materials have become potential thermoelectric materials due to their rich raw material reserves, low toxicity, and excellent electrical and thermal properties. In this study, a series of Cu1.8–x Sbx S (x = 0, 0.005, 0.02, 0.03, 0.04) bulk materials is synthesized by using mechanical alloying combined with spark plasma sintering process. This preparation method can shorten the preparation cycle of materials, and effectively improve the research and development efficiency of thermoelectric (TE) materials due to its simple process. The effects of different Sb doping amounts on the structure, micromorphology, and thermoelectric transport properties of Cu1.8–x Sbx S phase are investigated. The results show that when 0 ≤ x < 0.02, the bulk samples are single-phase Cu1.8S. With the further increase of Sb doping to 0.02 ≤ x ≤ 0.04, the second phase CuSbS2 is formed when Sb content exceeds the solid solubility limit of x = 0.02 in Cu1.8S, all Cu1.8–x Sbx S bulk samples exhibit p-type conductivity characteristics. Benefitting from the synergistic phonon scattering effect by multiscale defects, such as point defects (\begin{document}${\rm{Sb}}_{{\rm{Cu}}}^{ \bullet\bullet }$\end{document}, \begin{document}$ {\rm{V}}_{\rm{S}}^{ \bullet \bullet } $\end{document}), nanopores, secondary phases (CuSbS2), and dislocations, the thermal conductivity κ declines significantly from 1.76 W·m–1·K–1 (x = 0) to 0.99 W·m–1·K–1 at 723 K for the Cu1.76Sb0.04S sample. Finally, the peak dimensionless TE figure of merit (ZT ) value of 0.37 is achieved at 723 K for Cu1.77Sb0.03S resulting from a low thermal conductivity of 1.11 W·m–1·K–1 combining an appropriate power factor of 563 μW·m–1·K–2, which is 12% higher than that (0.33) of pristine Cu1.8S. Although the Sb doped Cu1.8S-based samples have lower thermal conductivity κ, the reduced power factor cannot be offset by reducing the thermal conductivity κ, so the TE figure of merit (ZT ) value is not significantly improved. Therefore, there is still much room for improving the performance of Sb doped Cu1.8S-based thermoelectric material, and its thermoelectric performance can be further optimized through nano-second phase recombination, energy band engineering, and introducing multi-scale defects, etc. Our results suggest that the introduction of Sb into thermoelectric materials is an effective and convenient strategy to improve ZT value by reducing thermal conductivity κ.

Preparation and Thermoelectric Properties of Cu1.8S/CuSbS2 Composites

Phase Structure and Thermoelectric Properties of Cu<sub>1.8–<i>x</i></sub> Sb<i><sub>x</sub></i> S Thermoelectric Material

Phase structure and thermoelectric properties of Cu<sub>1.8-<i>x</i></sub>Sb<i><sub>x</sub></i>S thermoelectric material

Phase Stability, Crystal Structure and Thermoelectric Properties of Cu Doped AgSbTe2

Highly Enhanced Thermoelectric and Mechanical Properties of Bi-Sb-Te Compounds by Carrier Modulation and Microstructure Adjustment

Effects of Sb Deviation from Its Stoichiometric Ratio on the Micro- and Electronic Structures and Thermoelectric Properties of Cu12Sb4S13.

Enhanced Thermoelectric Performance of Bi–Se Co-Doped Cu1.8S Via Carrier Concentration Regulation and Multiscale Phonon Scattering

Enhanced Thermoelectric Properties Of Cu3sbse3-Based Composites With Inclusion Phases

Enhanced Thermoelectric Properties of MnxCu1.8S Via Tuning Band Structure and Scattering Multiscale Phonons

Enhancing thermoelectric performance of Cu1.8S by Sb/Sn co-doping and incorporating multiscale defects to scatter heat-carrying phonons

High Thermoelectric Figure of Merit Achieved in Cu2S1-xTex Alloys Synthesized by Mechanical Alloying and Spark Plasma Sintering

Enhanced Thermoelectric Performance of Bi–Se Co-Doped Cu 1.8 S via Carrier Concentration Regulation and Multiscale Phonon Scattering

Effects of sintering temperature on thermoelectric properties of Cu1.8S bulk materials

Bi and Sn Co-Doping Enhanced Thermoelectric Properties of Cu3SbS4 Materials with Excellent Thermal Stability.

High Thermoelectric Performance Balanced by Electrical and Thermal Transport in Tetrahedrites Cu12+xSb4S12Se

Optimal performance of Cu1.8S1−xTex thermoelectric materials fabricated via high-pressure process at room temperature

Optimal Performance of Cu 1.8 S 1− X Te X Thermoelectric Materials Fabricated Via High-Pressure Process at Room Temperature

Significant improvement in the thermoelectric performance of Sb-incorporated chalcopyrite compounds Cu18Ga25SbxTe50−x (x = 0–3.125) through the coordination of energy band and crystal structures

Realizing the Ultralow Lattice Thermal Conductivity of Cu3SbSe4 Compound via Sulfur Alloying Effect

Nanostructured Bi2-Xcuxs3 Bulk Materials With Enhanced Thermoelectric Performance

The Effect of Te Substitution for Sb on Thermoelectric Properties of Tetrahedrite