Abstract:Thin-gauge non-oriented silicon steel with high strength was successfully processed using strip casting. Texture evolution and strengthening mechanism via nanoscale Cu-rich precipitates were studied to fundamentally understand the balanced combination of magnetic properties and mechanical properties. Coarse equiaxed grains with average size of ∼190 μm and relatively random texture were formed in the as-cast strip, which contributed to the inhomogeneous deformation, resulting in high density of shear bands. Exact Cube was retained from the initial Cube texture and new Goss was formed during the heavy rolling process in the 0.20 mm cold rolled sheet, which promoted relatively strong Cube and Goss texture after recrystallization annealing. The 0.20 mm annealed sheet exhibited high magnetic induction of 1.709 T, which corresponds to the high texture factor of 0.5. The total iron losses were significantly reduced with decrease in thickness, and the P1.5/50, P1.0/400, and P1.0/1000 in 0.20 mm sheet were as low as 2.63, 15.17 and 55.63 W/kg, respectively, which showed a good match between magnetic induction and iron loss. During the aging process, both the magnetic induction and total iron loss exhibited relatively good stability. With increase in aging time, the yield strength first rapidly increased and then slightly decreased. In 0.20 mm sheet, peak yield strength of ∼630 MPa was obtained on aging at 550 °C for 90–120 min. The key mechanism of precipitation strengthening was attributed to the difference in modulus and coherency strain associated with high density of nanoscale precipitates of ∼5 nm. The study revealed that the nanoscale Cu-rich precipitates can be adopted as effective approach to increase the yield strength over ∼100 MPa without deteriorating iron loss in thin-gauge non-oriented silicon steel by strip casting, which guaranteed the balance of magnetic properties and mechanical properties to meet the requirements of high-speed motor.

Practice on a High Carbon High Strength Steel Produced by Compact Strip Production

The CSP Process Development of the Press Hardening Steel

Solidification Structure of Low Carbon Steel Strips with Different Phosphorus Contents Produced by Strip Casting

Microstructure and Mechanical Properties of Hot-rolled 65mn Steel Produced by CSP

Microstructural evolution and grain refinement of a high strength low alloy steel produced by compact strip production

Mechanical Properties of Heat Treated 65mn Steel Produced by Compact Strip Production

Hot Ductility of High Carbon Steel Produced by Csp

CCT Diagram and Hardenability of 65mn Steel Produced by Compact Strip Production

Mechanical properties and strengthening mechanism of high-strength low-carbon automobile steel plates produced by CSP technology

Precipitates in High Strength Hot-rolled Strip for Automobile Pilot Produced by CSP Technology

Microstructure and mechanical properties of a hot-rolled 30CrMo steel produced by compact strip production

Microstructures and Mechanical Properties of Low Carbon Steel Hot Rolled in Ferrite Region Based on CSP Line

A simple route for preparation of TRIP-assisted Si–Mn steel with excellent performance using direct strip casting

The Effect of Relaxing on the Grain Refinement of Low Carbon High Strength Microalloyed Steel Produced by Compact Strip Production

Mechanical Properties of Heat Treated 30crmo Steel Produced by Compact Strip Production

A Simple Method to Produce Austenite-Based Low-Density Fe–20Mn–9Al–0.75C Steel by a Near-Rapid Solidification Process

Microstructure Characteristics and Strengthening Behavior of Cu-Bearing Non-Oriented Silicon Steel: Conventional Process versus Strip Casting

Thin-gauge non-oriented silicon steel with balanced magnetic and mechanical properties processed by strip casting

Tem Observation on Nano-Precipitation of Plain Low Carbon Steel by Csp

Carbides/Nitrides Precipitates in A C-Mn Strip by Csp Technology