Effect of TiB 2 content on microstructure and mechanical properties of GH3536 superalloy formed by laser solid forming
Jiaying Gao,Fenggang Liu,Lixin Liu,Fencheng Liu,Qifan You,Yongsheng Zheng,Pengfei Wang,Hao Qiu
DOI: https://doi.org/10.1016/j.mtcomm.2023.107168
IF: 3.8
2023-09-28
Materials Today Communications
Abstract:In this paper, GH3536 and TiB 2 /GH3536 alloys were prepared by laser solid forming(LSF). The effects of TiB 2 content on the microstructure and mechanical properties of as-deposited samples were investigated. The results show that, with the increase of TiB 2 content in the as-deposited samples, the molten pool boundary becomes shallower, the dendrite structure grows coarser, and the grain size gets larger. Meanwhile, phase segregation intensifies at the interdendritic and grain boundaries. The shape and types of the precipitated phases change significantly: the strip M 23 C 6 carbide phase progressively evolves into a network phase of M 23 C 6 carbide, M 2 B boride, and Mo-rich phase. Besides, the grain size of the solid-solution samples becomes smaller, and the columnar grains in both sample groups tend to be equiaxed. Interdendritic precipitates undergo a morphological change from a continuous network to a granular one as they gradually dissolve into the matrix. The microhardness of both sample groups also rises, and their elongation gradually declines as the amount of TiB 2 increases. However, the tensile strength trend exhibits the opposite fluctuation, as the tensile strength of as-deposited samples drops and that of solid-solution samples increases with the increase of TiB 2 content.
materials science, multidisciplinary