Abstract:Alkali metal salts (AMS) promoted MgO with high CO2 uptakes represents a promising adsorbent candidate for CO2 capture. The AMS-MgO composite adsorbents are facing the challenges of increased pressure drop or elutriation when employed in dual fixed-bed reactor or twin circulating fluidized-bed configurations. Granulation by the extrusion-spheronization technique represents an effective problem-solving strategy. However, textural properties and CO2 uptakes of MgO-based adsorbent pellets might be adversely affected by the granulation process. In this work, AMS-MgO composite adsorbent pellets were prepared by the extrusion-spheronization method. Citric acid (CA), ammonium bicarbonate (AB), urea (UA) and microcrystalline cellulose (MC) were employed as pore-forming templates to improve the porous structures and CO2 uptakes of the AMS-MgO pellets. CO2 uptakes and adsorption kinetics of the adsorbent pellets were studied using a fixed-bed reactor. Effects of granulation and pore templating on the structure-performance relationships of the AMS-MgO pellets were unraveled. Granulation had resulted in the remarkable decrease in CO2 uptake from 10.87 to 4.24 mmol CO2/g due to the impaired textural parameters. The employed sacrificial templates endowed the AMS-MgO pellets with enhanced CO2 uptakes and improved carbonation kinetics. This was associated with extended surface area and expanded pore structures due to gas liberation in the pyrolysis of templates, which had facilitated the kinetics of CO2 bulk diffusion. The desired AMS-MgO-MC pellet modified with MC template showed a high CO2 uptake of 7.54 mmol CO2/g in 50%CO2 at 340 °C, and its CO2 uptake was stabilized around 5.0 mmol CO2/g within 20 cycles. Besides, the AMS-MgO-MC pellet also exhibited good mechanical properties. The results will guide the rational design of highly efficient and robust MgO-based adsorbent pellets for CO2 capture applications.

Recycle of Cotton Waste by Hard Templating with Magnesium Acetate As MgO Precursor.

Synthesizing nanocrystal-assembled mesoporous magnesium oxide using cotton fibres as exotemplate

Preparation of Al2O3-MgO Acid/Base Bifunctional Material with High Specific Surface Area Using Degreasing Cotton As Exotemplate

Preparation of Al_2O_3-MgO Acid/Base Bifunctional Material with High Specific Surface Area Using Degreasing Cotton as Exotemplate

Preparation and Characterization of Activated Carbon Fiber (ACF) from Cotton Woven Waste

Preparation of hollow MgO nanosorbents via the templating method and study of their adsorption mechanism

Porous Carbon Material based on Biomass Prepared by MgO Template Method and ZnCl2 Activation Method as Electrode for High Performance Supercapacitor

Preparation of a N-P co-doped waste cotton fabric-based activated carbon for supercapacitor electrodes

Preparation of Shaped Magnesium Oxide/carbon Catalysts Using Rice Grains As an Exotemplate and Carbon Precursor

Unravelling the pore templating effect on CO2 adsorption performance of alkali metal nitrates promoted MgO pellets

Preparation of activated carbon fabrics from cotton fabric precursor

Effects of Temperature and Mg-Based Additives on Properties of Cotton Stalk Torrefaction Products

Pyrolysis Behavior and Pore-Forming Mechanism During Reuse of Textile Waste Flax by Activation

In Situ Synthesis of Ordered Mesoporous Silica Materials Embedded in Cotton Fiber and Their Co2 Capture Properties

Synthesis and characterization of modified activated carbon (MgO/AC) for methylene blue adsorption: optimization, equilibrium isotherm and kinetic studies

Textile Waste-Derived Cobalt Nanoparticles Embedded in Active Carbon Fiber for Efficient Activation of Peroxymonosulfate to Remove Organic Pollutants

Utilization of Waste Cotton Fibers by Extracting Nanocellulose Crystals: A Study on Phosphoric Acid Method Compared with Sulfuric Acid Method and TEMPO Oxidation Method

Application of carbon-doped nano-magnesium oxide for catalytic ozonation of real textile wastewater: fractional factorial design and optimization

Influence of torrefaction with Mg-based additives on the pyrolysis of cotton stalk

The alkaline sites integrated into biomass-carbon reinforce selective adsorption of acetic acid: In situ implanting MgO during activation operation

Activated carbon fibers from recycled acrylic and cotton for carbon dioxide capture