Influence of Al content on microstructure and nanoindentation of selective laser melting Al<i><sub>x</sub></i>CoCrFeNi (<i>x</i>=0.3,0.5,0.7,1. 0)
Cao Deng,Ruidi Li,Tiechui Yuan,Pengda Niu
DOI: https://doi.org/10.11868/j.issn.1001-4381.2021.000737
2022-01-01
Journal of Materials Engineering
Abstract:AlxCoCrFeNi(x = 0, 3, 0, 5, 0, 7, 1, 0) high-entropy alloy was fabricated by selective laser melting (SLM), and pre-alloyed powder was prepared by gas atomization. The phase composition, microstructure, hardness, Young's modulus and creep curve of AlxCoCrFeNi were comprehensively analyzed through X-ray diffractometer,, scanning electron microscope and nanoindentation experiments, respectively. The influence of Al content on the microstructure and nanoindentation of AlxCoCrFeNi was discussed. The results show that Al0.3 CoCrFeNi and Al-0.5 CoCrFeNi are FCC structure, while Al-0.3 CoCrFeNi and Al-0.5 CoCrFeNi are BCC/B2 structure. The microstructure of Al-0.3 CoCrFeNi and Al-0.5 CoCrFeNi are mainly composed of equiaxed crystals, while Al-0.7 CoCrFeNi and Al1.0CoCrFeNi are mainly composed of columnar crystals. It indicates that the content of Al has great influence on the microstructure of AL CoCrFeNi high-entropy alloy. With the increase of Al content, defects such as pores and cracks in the specimens increase. There is no obvious molten pool morphology observed in Al-0.3 CoCrFeNi and Al-0.5 CoCrFeNi. The residual stress increases with the increase of Al content. The hardness and Young' s modulus of the samples were measured. It was found that with the increase of Al content, the hardness of the sample increases from 447HV to 567HV. The Young' s modulus of Al0.3 CoCrFeNi is about 273 GPa, and Al-0.5 CoCrFeNi is about 233 GPa, while Al-0.7 CoCrFeNi and Al-1.0 CoCrFeNi are about 240 GPa and 242 GPa, respectively. The changes in hardness and Young's modulus are mainly related to the microstructure and phases of specimens. Different from the traditional creep curve, the creep curve of Al-x CoCrFeNi includes only two stages, which are instantaneous creep and steady-state creep. The creep mechanism is mainly dislocation creep. Among the samples, Al-0.7 CoCrFeNi has the best creep resistance. Al-0.3 CoCrFeNi has the best print formability, with the yield strength of 702 MPa, and the elongation is 27. 5 %.