Elinvar effect in severely-deformed Ti-50.8(at%)Ni thin belt

Y.W Song,Mingjiang Jin,Shungui Zuo,Xuejun Jin

DOI: https://doi.org/10.1016/j.matlet.2019.05.109

IF: 3

2019-01-01

Materials Letters

Abstract:•Ti-50.8 (at%) Ni alloy was severely deformed followed by low temperature aging.•Elinvar effect was observed over a wide temperature range.•Elinvar effect was related to softening of the nanodomains.

What problem does this paper attempt to address?

Elinvar property of cold-rolled NiTi alloy

Zhongzheng Deng,Kangjie Chu,Qiao Li,Yusuke Onuki,Qingping Sun

DOI: https://doi.org/10.1016/j.scriptamat.2020.05.058

IF: 6.302

2020-10-01

Scripta Materialia

Abstract:We tailor the temperature dependence of elastic modulus (TDEM) of polycrystalline NiTi plates by cold rolling up to 60% thickness reduction. In-plane Elinvar property is obtained with a low elastic modulus temperature coefficient of 6.0 × 10−5 K−1 over a temperature range of 192 K. The microstructure mainly consists of approximately equal volume fractions of {111}<uvw>-oriented B2 and {102}<uvw>-oriented B19′ nanocrystals of high thermal stability due to defect pinning and grain refinement. The opposite TDEMs of the two phases can compensate each other and cause the Elinvar behavior. Such mechanism can also be used to obtain Elinvar property for other shape memory alloys.</uvw></uvw>

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering
Influence of aging temperature on physical properties of a 40NiCrTiAl Elinvar alloy

Xiangyu Xu,Jianyin Weng,Xuemin Wang,Jinghua Cong,Chengjia Shang

DOI: https://doi.org/10.1007/s10853-024-10358-4

IF: 4.5

2024-10-30

Journal of Materials Science

Abstract:This study investigates the effect of aging temperature on the physical properties of Fe–40.32Ni–5.51Cr–2.63Ti–0.47Al–0.55Mn–0.40Si–0.016C (wt.%) alloy using scanning electron microscopy, transmission electron microscopy, X-ray diffraction, a physical-property measurement system, and a dilatometer, among others. After a solution treatment, the microstructure of the experimental alloy was composed of the γ phase. The aging process involved the precipitation of the γ ' and η phases to regulate the Elinvar effect. No martensite or ferrite phases were observed in either the solid-solution or aged samples using X-ray diffraction and transmission electron microscopy. The Elinvar effect for traditional Fe–Ni–Cr ferromagnetic Elinvar alloys is related to spontaneous magnetisation, resulting in spontaneous volume magnetostriction. The inflection temperature of the elastic modulus exceeded the Curie temperature. The larger the precipitation amount, the weaker the ΔE effect, and the larger the Young's modulus value. For a holding time of 2 h, the amount of precipitation was maximised at an aging temperature of 650 °C, while Young's modulus and its temperature coefficient achieved maxima of 190 GPa and 9.0 × 10− 5 °C− 1 , respectively. In addition, the lattice constant at room temperature indirectly reflects the amount of precipitation. Young's modulus, the temperature coefficient of Young's modulus, the Curie temperature, and the linear-expansion coefficient obeyed an approximately parabolic law as functions of the lattice constant or its reciprocal. Moreover, Young's modulus and its temperature coefficient can be estimated using the Curie temperature and linear-expansion coefficient, respectively.

materials science, multidisciplinary
Elinvar Effect in Co-doped TiNi Strain Glass Alloys

Jian Cui,Xiaobing Ren

DOI: https://doi.org/10.1063/1.4893003

IF: 4

2014-01-01

Applied Physics Letters

Abstract:Elinvar effect is observed in non-magnetic Co doped TiNi strain glass alloys. The Elinvar effect is explained by the coupling of dynamic size effect and size dependence of elastic modulus. The appearance of Elinvar effect is highly correlated with the nucleation size, so that only for strain glass with high point defect concentration, Elinvar effect can be observed. Due to the generality of size dependence of elastic modulus, Elinvar effect is expected to be observed in many other strain glass materials, which points out a way to find new Elinvar materials.
Tuning temperature coefficient of elastic modulus by heat treatment in a compositionally-modulated Ti-Nb-based alloy

Delun Gong,Haoliang Wang,Qiushuang Wang,Shujun Li,Kun Lin,Yandong Wang,Rui Yang,Yulin Hao

DOI: https://doi.org/10.1016/j.scriptamat.2022.115275

IF: 6.302

2023-01-05

Scripta Materialia

Abstract:Temperature coefficient of elastic modulus can be positive for metastable β phase in titanium alloys whereas the precipitation of α phase from the β matrix phase results in a negative coefficient. This abrupt transition inspires us to tune the coefficient from positive, via zero of Elinvar effect, to negative by aging treatment in a Ti-Nb-based alloy. Here reports that its coefficients are continuously tunable by a compositionally-modulated β+α" dual-phase microstructure induced by spinodal decomposition. As the aging time increases at 723 K, the coefficient keeps positive almost unchanged initially, then drops quickly toward zero, and finally decreases slowly of being negative. A mixture rule modeling suggests that the coefficients of both phases decrease gradually from positive of being metastable to negative of being stable. These findings provide a new strategy to achieve Elinvar effect by optimizing the compositionally-modulated microstructure via heat treatments.

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering
Inverse Elastocaloric Effect in a Ti-Ni Alloy Containing Aligned Coherent Particles of Ti3Ni4

Fei Xiao,Takashi Fukuda,Tomoyuki Kakeshita

DOI: https://doi.org/10.1016/j.scriptamat.2016.07.016

IF: 6.302

2016-01-01

Scripta Materialia

Abstract:We have detected an inverse elastocaloric effect in a Ti-51Ni (at%) alloy which contains aligned coherent particles of Ti3Ni4 formed by aging under tensile stress. In this alloy, the temperature of the specimen decreases when stress is applied due to a stress-induced reverse martensitic transformation (from the R-phase to the B2-phase) The temperature decrease caused by this effect is about 1.1K at 300K. The internal stress field around the Ti3Ni4 precipitate is responsible for this effect. A further increase in the tensile stress causes a temperature rise due to a conventional elastocaloric effect.
Deformation Temperature and Postdeformation Annealing Effects on Severely Deformed TiNi Alloy by Equal Channel Angular Extrusion

Zhenhua Li,Xianhua Cheng

DOI: https://doi.org/10.1016/s1005-8850(07)60123-6

2007-01-01

Abstract:Micron TiNi alloy blocks were fabricated at high temperature by equal channel angular extrusion (ECAE) using hotforged Ti-50.3at%Ni alloy as the raw material and the effects of deformation temperature and postdeformation annealing on the severely deformed TiNi alloy by ECAE were investigated. The results show that the TiNi alloy processed by ECAE undergoes severe plastic deformation, and lowering the deformation temperature and increasing the number of extrusions contribute to grain refinement. When the annealing temperature is below 873 K, static recovery is the main restoration process; when the temperature rises to 973 K, static recrystallization occurs. It is found that fine particles are precipitated when the TiNi alloy processed by ECAE is annealed at 773 K.
A New Mechanism for Low and Temperature-Independent Elastic Modulus

Liangxiang Zhang,Dong Wang,Xiaobing Ren,Yunzhi Wang

DOI: https://doi.org/10.1038/srep11477

IF: 4.6

2015-01-01

Scientific Reports

Abstract:The first Elinvar alloy, FeNiCr, which has invariant elastic modulus over a wide temperature range, was discovered almost 100 years ago by Guillaume. The physical origin of such an anomaly has been attributed to the magnetic phase transition taking place in the system. However, the recent discovery of non-magnetic Elinvar such as multi-functional β-type Ti alloys has imposed a new challenge to the existing theories. In this study we show that random field from stress-carrying defects could suppress the sharp first-order martensitic transformation into a continuous strain glass transition, leading to continued formation and confined growth of nano-domains of martensite in a broad temperature range. Accompanying such a unique transition, there is a gradual softening of the elastic modulus over a wide temperature range, which compensates the normal modulus hardening due to anharmonic atomic vibration, resulting in a low and temperature-independent elastic modulus. The abundance of austenite/martensite interfaces are found responsible for the low elastic modulus.
Elastocaloric Effect Induced by the Rubber-Like Behavior of Nanocrystalline Wires of A Ti-50.8ni (at.%) Alloy

Xiao Liang,Fei Xiao,Mingjiang Jin,Xuejun Jin,Takashi Fukuda,Tomoyuki Kakeshita

DOI: https://doi.org/10.1016/j.scriptamat.2017.02.026

IF: 6.302

2017-01-01

Scripta Materialia

Abstract:Elastocaloric effects in shape memory alloys are usually caused by latent heat associated with the stress-induced martensitic transformation. We report here that the rubber-like behavior of the R-phase in nanocrystalline Ti-50.8Ni (at.%) wires, realized by an aging heat treatment under tensile stress, also contributes a significant elastocaloric effect. The efficiency of the elastocaloric effect caused by the rubber-like behavior is higher than that caused by the stress-induced B2↔B19′ transformations because of the small energy dissipation. The usage of the rubber-like behavior is a method to extend the temperature window of the elastocaloric effect in shape memory alloys.
Orientation Dependence of Elastocaloric Effect in an Aged Ni-rich Ti-Ni Alloy

Fei Xiao,Xiao Liang,Hong Chen,Zhenxing Li,Zhu Li,Xuejun Jin,Takashi Fukuda

DOI: https://doi.org/10.1016/j.scriptamat.2019.04.030

IF: 6.302

2019-01-01

Scripta Materialia

Abstract:Elastocaloric effects caused by the stress-induced B2-R and the reverse martensitic transformations (B2: the parent phase, R: the martensite phase) were studied by using an aged single crystal of Ti-50.8Ni shape memory alloy including coherent precipitates of Ti3Ni4. Inverse elastocaloric effect was observed when tensile stress is applied in the [100]B2 direction, while conventional one was observed in the [111]B2 direction. This result implies that transformation strain in the [100]B2 direction is negative for any variants.
Resolution of a Discrepancy of Magnetic Mechanism for Elinvar Anomaly in Fe-Ni Based Alloys

Fangyu Qin,Wenlong Xiao,Fengshuang Lu,Yuanchao Ji,Xinqing Zhao,Xiaobing Ren

DOI: https://doi.org/10.1016/j.jmst.2018.09.032

2018-01-01

Journal of Material Science and Technology

Abstract:Fe-Ni based Elinvar alloys performing temperature-independent elastic modulus over a wide temperature range have found wide and significant applications. Although numerous models involved with magnetism have been proposed to explain the Elinvar anomaly, some of the puzzles concerning the anomaly have not been fully understood. In this work, a remarkable discrepancy between the inflection temperature of modulus and the Curie temperature in a typical Fe-Ni-Cr Elinvar alloy was found,challenging the magnetic mechanism for Elinvar anomaly. Microstructural characterization and dynamic mechanical analysis demonstrate the occurrence of a strain glass transition with continuous formation of nanodomains. Accompanying such a transition, the gradual softening in the elastic modulus of austenite offsets the modulus hardening due to the vibrational anharmonicity of nanodomains upon cooling, leading to the Elinvar effect. As a result, the inflection temperature of modulus corresponds to the initiation of nanodomains’ formation instead of magnetic transition. Our findings specify the association of Elinvar anomaly with structural aspects, and provide new insights into the mechanism of Elinvar anomaly in Fe-Ni based alloy.
Microstructural Origin of Ultrahigh Damping Capacity in Ni50.8 Ti49.2 Alloy Containing Nanodomains Induced by Insufficient Annealing and Low-Temperature Aging

Yuanwei Song,Mingjiang Jin,Xiaocang Han,Xiaodong Wang,Peng Chen,Xuejun Jin

DOI: https://doi.org/10.1016/j.actamat.2020.116541

IF: 9.4

2021-01-01

Acta Materialia

Abstract:We report a Ni50.8Ti49.2 alloy that exhibits an ultrahigh damping capacity with an internal friction (IF) value of ~ 0.35 (tan δ) at low frequencies in a wide temperature range. This alloy undergoes low-temperature aging (LTA) after insufficient annealing from a severely deformed state (~90% cold work). Via phase transformation (PT) analyses and microstructure characterization, we demonstrate that this high broad IF plateau originates from nanodomains and the stable coexistence of the B19’- and R-phases over a wide temperature range. The abundant phase boundaries (PBs) and movable interfaces between nanodomains contribute significantly to this high broad IF plateau. Further analyses validate the critical role of LTA in inducing nanodomains, i.e., resulting in localized Ni segregation. The abnormal appearance of needle-like B19’- martensites near room temperature is attributed to the defects that remain after insufficient annealing, after which LTA promotes localized depletion or enrichment of Ni. In addition, the results of this study indicate that high density nanodomains are generated from the two steps of insufficient annealing and LTA in the severely deformed Ni50.8Ti49.2 alloy. The idea of a high-damping microstructure design based on “domain engineering” is realized.
Stable and Large Superelasticity and Elastocaloric Effect in Nanocrystalline Ti-44Ni-5Cu-1Al (at%) Alloy

Hong Chen,Fei Xiao,Xiao Liang,Zhenxing Li,Xuejun Jin,Takashi Fukuda

DOI: https://doi.org/10.1016/j.actamat.2018.08.003

IF: 9.4

2018-01-01

Acta Materialia

Abstract:Superelastic behavior and elastocaloric effect were investigated in a Ti-44Ni-5Cu-1Al (at%) alloy subjected to various thermomechanical treatments. The specimen heat-treated at 673 K for 5 min after hot rolling and subsequent cold rolling exhibited excellent superelastic strain of 4.9% with a small stress hysteresis of 90 MPa when the maximum tensile stress was 500 MPa. This specimen also exhibited a large elastocaloric effect with a temperature decrease of 17 K when the stress of 500 MPa was removed adiabatically. No remarkable deterioration was observed for the superelastic strain and elastocaloric effect up to 5000 mechanical cycles. The maximum superelastic strain obtained was 6.8% under a tensile stress of 750 MPa. Transmission electron microscope observation and in-situ X-ray diffraction analysis under tensile stress revealed that the average grain size of the specimen is about 40 nm, and the specimen exhibits a successive B2-B19-B19' transformation. (C) 2018 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Revealing the Superior Post-Necking Elongation in the Fine-Grained Ti-6Al-4V ELI at Cryogenic Temperature

Quan Gao,Rengeng Li,Hao Wu,Kesong Miao,He Wu,Chenglu Liu,Xuewen Li

DOI: https://doi.org/10.3390/met14050600

IF: 2.695

2024-05-21

Metals

Abstract:The mechanical properties of a fine-grained (FG) Ti-6Al-4V extra-low interstitial (ELI) alloy were investigated by tensile tests at 298 K and 77 K. The experimental results indicated that, at 77 K, the alloy exhibits a small uniform elongation of 2.65%, but has a fracture elongation of 19.2%, showing superior post-necking elongation. At 298 K, the alloy displays a single dislocation slipping, β→α′′ phase transformation occurred, and 6.35% uniform elongation was obtained, whereas the coupling of dislocation slipping and twinning deformation behaviors dominated at 77 K. The limited uniform elongation is attributed to the absence of martensite phase transformation at 77 K, whereas the decent fracture elongation is ascribed to the resistance offered by twinning against plastic instability.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Deformation Dependence of Transformation Behavior of Ti-Ni-Nb Wide Hysteresis Shape Memory Alloy

He Xiangming,Rong Lijian,Yan Desheng,Li Yiyi

DOI: https://doi.org/10.3321/j.issn:1002-185X.2006.02.014

2006-01-01

Rare Metal Materials and Engineering

Abstract:This work is to systemically study the effect of deformation on the stress-induced martensitic transformation behavior of Ti44Ni47Nb9 alloy by performing differential scanning calorimetry (DSC) and cryogenic tensile tests at a temperature of (M-s+30(degrees)C). DSC measurements showed that the process of stress-induced martensitic transformation had been completed as the specimen was deformed to about 14% of strain in tension. The reverse transformation temperature interval of the stress-induced martensite is much smaller than that of the thermally induced martensite. The experimental results also indicated that A(s) temperature of the reverse transformation, the reverse transformation temperature interval and the transformation heat of the deformed specimen associated with the stress-induced martensite are increased with increasing of the level of deformation. However, the wide hysteresis effect due to the deformation vanished after heating. The transformation heat and the forward transformation start temperature of the subsequent cooling are decreased slightly with increasing of strain.
Elinvar effect in $β-$Ti simulated by on-the-fly trained moment tensor potential

Alexander V. Shapeev,Evgeny V. Podryabinkin,Konstantin Gubaev,Ferenc Tasnádi,Igor A. Abrikosov

DOI: https://doi.org/10.1088/1367-2630/abc392

2020-05-09

Abstract:A combination of quantum mechanics calculations with machine learning (ML) techniques can lead to a paradigm shift in our ability to predict materials properties from first principles. Here we show that on-the-fly training of an interatomic potential described through moment tensors provides the same accuracy as state-of-the-art {\it ab inito} molecular dynamics in predicting high-temperature elastic properties of materials with two orders of magnitude less computational effort. Using the technique, we investigate high-temperature bcc phase of titanium and predict very weak, Elinvar, temperature dependence of its elastic moduli, similar to the behavior of the so-called GUM Ti-based alloys [T. Sato {\ it et al.}, Science {\bf 300}, 464 (2003)]. Given the fact that GUM alloys have complex chemical compositions and operate at room temperature, Elinvar properties of elemental bcc-Ti observed in the wide temperature interval 1100--1700 K is unique.

Materials Science,Computational Physics
Strain Glass Transition in a Multifunctional Β-Type Ti Alloy

Yu Wang,Jinghui Gao,Haijun Wu,Sen Yang,Xiangdong Ding,Dong Wang,Xiaobing Ren,Yunzhi Wang,Xiaoping Song,Jianrong Gao

DOI: https://doi.org/10.1038/srep03995

IF: 4.6

2014-01-01

Scientific Reports

Abstract:Recently, a class of multifunctional Ti alloys called GUM metals attracts tremendous attentions for their superior mechanical behaviors (high strength, high ductility and superelasticity) and novel physical properties (Invar effect, Elinvar effect and low modulus). The Invar and Elinvar effects are known to originate from structural or magnetic transitions, but none of these transitions were found in the GUM metals. This challenges our fundamental understanding of their physical properties. In this study, we show that the typical GUM metal Ti-23Nb-0.7Ta-2Zr-1.2O (at%) alloy undergoes a strain glass transition, where martensitic nano-domains are frozen gradually over a broad temperature range by random point defects. These nano-domains develop strong texture after cold rolling, which causes the lattice elongation in the rolling direction associated with the transition upon cooling and leads to its Invar effect. Moreover, its Elinvar effect and low modulus can also be explained by the nano-domain structure of strain glass.
Analysis of Mechanical-Thermal Coupled Experiments of Single Crystal TiNi Alloys

LIN Yin,YAN Yan,LI Chong-he,ZHU Ming,HUO Yong-zhong

DOI: https://doi.org/10.3969/j.issn.0254-0053.2012.03.004

2012-01-01

Abstract:The mechanic properties in the Ti-50.0at%Ni single crystals were studied,The crystals were prepared by means of improved Bridgeman method of unidirectional solidification technology.Analysis of mechanical-themal coupled experimental curves was performed and the variational discipline of the parameters were summarized by fitting the curves.The maximum tensile recoverable strain of the single crystal was 10.83%,which is very close to the theoretical maximum.There was no strengthen phase in the matrix of equiatomic TiNi single crystal,thus the plastic deformation yield strength of the alloy is very low and the specimen has slipped before the stress reached the critical stress of stress-induced martensitic transformation.Therefore,above the Af point,only part of the superelasticity was exhibited since irreversible plastic deformation was introduced.
The Microstructure and Linear Superelasticity of Cold-Drawn TiNi Alloy

YF Zheng,BM Huang,JX Zhang,LC Zhao

DOI: https://doi.org/10.1016/s0921-5093(99)00632-2

2000-01-01

Abstract:The microstructure and linear superelasticity of cold-drawn TiNi alloy have been investigated using CTEM, HREM and in-situ transition electron microscopy observations and tensile tests. The microstructural evolution procedure of the martensite variants with increasing degree of area reduction was found to be that the quantities of (111̄) Type I, (001) compound, (011) Type I and (111) Type I twinning plates increase gradually with decreasing the amount of the 〈011〉 Type II twinning bands. The corresponding dominant deformation mechanism changed from the coalescence of martensite variants to the reorientation of substructural bands inside martensite variants utilizing the most favorably oriented twin systems. The intrinsic reason for the linear superelasticity of the moderately cold-drawn TiNi alloy was confirmed to be associated with the appearance and disappearance of (001) microtwinning inside the 〈011〉 Type II substructural bands.
Multifunctional nanostructured NiTi alloy with Invar, Elinvar and Rinvar properties

Zhongzheng Deng,Qiao Li,Yusuke Onuki,Qingping Sun

DOI: https://doi.org/10.1016/j.jallcom.2022.164682

IF: 6.2

2022-07-01

Journal of Alloys and Compounds

Abstract:A multifunctional NiTi alloy with Invar (dimension-invariant), Elinvar (elastic modulus-invariant) and Rinvar (resistivity-invariant) properties over the temperature range from 125 K to 375 K is fabricated through cold rolling of 60% thickness reduction. The underlying microstructure of such multifunctional NiTi alloy mainly consists of B2 and B19′ nanocrystals which can continuously undergo a small fraction of thermally induced B2↔B19′ phase transition over a wide temperature range. Such phase transition can induce a negative thermal expansion to compensate for the positive expansions of the B2 and B19′ phases and thus yield the Invar property. Meanwhile, the opposite temperature dependences of elastic modulus of the B2 and B19′ phases can compensate each other and cause the macroscopic overall Elinvar property. In addition, the presence of nanocrystals enhances the negative temperature dependence of resistivity (TDR) caused by boundary scattering, which compensates for the positive TDR due to background scattering and thus leads to the Rinvar behavior. The three compensation mechanisms in the dual-phase nanostructure can also be exploited in other shape memory alloys to obtain the Invar, Elinvar and Rinvar properties so as to broaden their applications.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
Deformation phenomenon of P/M Ti-5Al-2.5Sn(ELI) alloy

Yinjiang Wu,Tao Lan,Lian Zhou,Zhihao Jin

2005-01-01

Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering

Abstract:The deformation properties of P/M Ti-5Al-2.5Sn (ELI) alloy has been studied by tensile test, TEM and SEM. The results show that Ti-5Al-2.5Sn (ELI) alloy existed features toothed stress-strain curve, multiple necking and non-uniform deformation under the cryogenic condition. It is related to the deformation phenomenon of twinning and dislocation slipping in the alloy.

Elinvar effect in severely-deformed Ti-50.8(at%)Ni thin belt

Elinvar property of cold-rolled NiTi alloy

Influence of aging temperature on physical properties of a 40NiCrTiAl Elinvar alloy

Elinvar Effect in Co-doped TiNi Strain Glass Alloys

Tuning temperature coefficient of elastic modulus by heat treatment in a compositionally-modulated Ti-Nb-based alloy

Inverse Elastocaloric Effect in a Ti-Ni Alloy Containing Aligned Coherent Particles of Ti3Ni4

Deformation Temperature and Postdeformation Annealing Effects on Severely Deformed TiNi Alloy by Equal Channel Angular Extrusion

A New Mechanism for Low and Temperature-Independent Elastic Modulus

Elastocaloric Effect Induced by the Rubber-Like Behavior of Nanocrystalline Wires of A Ti-50.8ni (at.%) Alloy

Orientation Dependence of Elastocaloric Effect in an Aged Ni-rich Ti-Ni Alloy

Resolution of a Discrepancy of Magnetic Mechanism for Elinvar Anomaly in Fe-Ni Based Alloys

Microstructural Origin of Ultrahigh Damping Capacity in Ni50.8 Ti49.2 Alloy Containing Nanodomains Induced by Insufficient Annealing and Low-Temperature Aging

Stable and Large Superelasticity and Elastocaloric Effect in Nanocrystalline Ti-44Ni-5Cu-1Al (at%) Alloy

Revealing the Superior Post-Necking Elongation in the Fine-Grained Ti-6Al-4V ELI at Cryogenic Temperature

Deformation Dependence of Transformation Behavior of Ti-Ni-Nb Wide Hysteresis Shape Memory Alloy

Elinvar effect in $β-$Ti simulated by on-the-fly trained moment tensor potential

Strain Glass Transition in a Multifunctional Β-Type Ti Alloy

Analysis of Mechanical-Thermal Coupled Experiments of Single Crystal TiNi Alloys

The Microstructure and Linear Superelasticity of Cold-Drawn TiNi Alloy

Multifunctional nanostructured NiTi alloy with Invar, Elinvar and Rinvar properties

Deformation phenomenon of P/M Ti-5Al-2.5Sn(ELI) alloy