Experiment Study on the Mechanical Properties and Constitutive Model of Grade 1960 Steel Wires under and after Elevated Temperatures
Zongxing Zhang,Yuxuan Xu,Yaohua Huang,Wei Chen,Ya Ni,Jihong Ye,Jian Jiang
DOI: https://doi.org/10.1016/j.jobe.2023.108318
IF: 7.144
2023-01-01
Journal of Building Engineering
Abstract:To investigate the effects of different temperatures and cooling patterns on the surface charac-teristics, failure modes and mechanical properties of steel wires, a total of 52 steel wires of grade 1960 under and after elevated temperatures were tested. Then, the influence mechanism of temperatures on mechanical properties was further revealed with the help of SEM fracture scanning. Furthermore, the laws of reduction coefficient of mechanical properties of steel wires under and after elevated temperatures were proposed. Finally, the equation of high temperature stress-strain curve of steel wires was constructed. The results showed that the surface colors of steel wires gradually deepened with the increase of temperature, and a mass of zinc oxide par-ticles appeared on the surface of steel wires at 500 degrees C, when the galvanized layer began shedding a lot. Meanwhile, the fracture shape of the specimens became obvious cup-cone, especially when the temperature exceeded 600 degrees C, the shape turned conical. In addition, the elastic modulus, yield strength and tensile strength of steel wires at 300 degrees C accounted for 85 %, 68 % and 74 % of the corresponding mechanical properties at room temperature, respectively. When the temperature exceeded 300 degrees C, the mechanical properties of steel wires would decrease significantly. For example, the ultimate strength of steel wire at 400 degrees C was only 53 % of that at room temperature. Nevertheless, the mechanical properties of steel wires after high temperature were basically unchanged before 300 degrees C. Similarly, the mechanical properties of steel wires gradually decreased after cooling by temperature action above 300 degrees C. For example, when the heating temperature was 600 degrees C, the ultimate strength was only 46 % of that at room temperature. Ultimately, comparing with the result of experimental and previous literature, the accuracy of the proposed formula for the reduction coefficient of high temperature mechanical properties and constitutive model of steel wire was verified. It is recommended to set the fire resistance temperature of steel wire inside the bridge cable at around 300 degrees C.