Recoverable and plastic strains generated by forward and reverse martensitic transformations under external stress in NiTi SMA wires

P. Šittner,E. Iaparova,O. Molnárová,O. Tyc,X. Bian,L. Kadeřávek,L. Heller

2024-06-21

Abstract:Superelastic NiTi 1 shape memory alloy (SMA) wire was subjected to thermomechanical loading tests in tension to evaluate stress and temperature conditions under which the wire deforms plastically. Although the alloy demonstrated a very high resistance to plastic deformation in both the austenite and martensite phases, incremental plastic strains were recorded whenever the B2 cubic to B19' monoclinic martensitic transformation (MT) took place under external stress. To shed light on the origin of the functional fatigue presumably originating from the accumulated plastic strains, special closed-loop thermomechanical loading tests were performed to evaluate recoverable and plastic strains generated by the forward and reverse MTs under external stress. These experiments revealed that both forward and reverse MTs generate well-defined incremental plastic strains only if they occur above certain stress thresholds. Specifically, the forward MT upon cooling under stresses up to 500 MPa does not produce plastic strain or lattice defects, whereas the reverse MT upon heating generates plastic strains even under stress as low as 100 MPa. It is proposed that plastic deformation generated by martensitic transformations under low stresses takes place by [100](001) dislocation slip in martensite and while under high stresses it occurs via kwinking deformation in martensite. The characteristic thresholds and magnitudes of plastic strains generated by the forward and reverse MTs define the functional fatigue limits for NiTi. Specifically, the stress-strain-temperature responses recorded in closed-loop thermomechanical tests remain stable if both forward and reverse MTs occur below these thresholds. Conversely, they become unstable and exhibit predictable ratcheting if the MTs exceed these thresholds.

Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the non - recoverable plastic strain generated during the martensitic phase transformation of nickel - titanium shape - memory alloy (NiTi SMA) under external stress and its influence on functional fatigue. Specifically, the research aims to:

1. **Understand the origin of plastic strain**: Through special closed - loop thermomechanical loading tests, study the recoverable and plastic strains generated respectively during forward and reverse martensitic phase transformations under external stress. These tests help to reveal the generation mechanism of plastic strain.

2. **Evaluate phase - transformation conditions**: Determine under which stress and temperature conditions NiTi alloys will undergo plastic deformation. Research shows that even in the austenite and martensite phases, the alloy exhibits a high resistance to plastic deformation, but incremental plastic strains are still recorded during the martensitic phase transformation.

3. **Explore the causes of functional fatigue**: It has been found that the plastic strain generated during the reverse martensitic phase transformation during heating is significantly greater than that generated during the forward martensitic phase transformation during cooling. Therefore, the reverse martensitic phase transformation is considered to be the main cause of functional fatigue in NiTi actuators.

4. **Propose a plastic - deformation mechanism**: The paper proposes that at low stress, the plastic deformation generated during the martensitic phase transformation mainly occurs through the [100](001) dislocation - slip mechanism; while at high stress, it occurs through the kink - deformation mechanism.

Through these studies, the author hopes to provide a theoretical basis for understanding and predicting the functional fatigue of NiTi alloys, thereby guiding the design and application of materials.