Abstract:This study compares the microstructure and tensile properties of Ti6Al4V components fabricated by laser direct metal deposition (LDMD) additive manufacturing (AM) in the transverse and longitudinal directions. The results show anisotropic tensile properties with the transverse direction having high tensile and fracture strengths and the longitudinal direction having a high elongation and reduction of cross section. The anisotropic mechanical properties are attributed to the anisotropic microstructural distribution. The transverse tensile specimen is composed of short columnar prior-β grains which grow perpendicular to the tensile direction, and have a lamellar structure. Along the β grain boundary, αGB and large α colonies were identified. However, the longitudinal specimen shows that the long β structure is parallel to the tensile axis and that the microstructure is composed of basket-woven α phases with shorter α plates and smaller colony sizes compared with those in the transverse specimen. The fracture mechanism induced by the anisotropic microstructure along the transverse and longitudinal directions was compared by examining the fracture process in real-time using uniaxial in-situ scanning electron microscopy (SEM) tensile testing. The results show that shear fracture, which is caused by the vertical β grain boundaries and large α colonies with long α plates, occurs in the transverse specimen. The shear mode is the main reason behind the enhanced tensile strength and fracture strength due to the high resistance to microcrack propagation. However, in the longitudinal specimens, symmetric necking behavior due to the fine α grains resulted in uniform deformation of the grains on both sides of the grain boundaries, inducing greater elongation.

Microstructure, Mechanical Properties and Strengthening Mechanisms of AlCu5MnCdVA Aluminum Alloy Fabricated by Selective Laser Melting

Selective Laser Melting of Al-Cu-Mn-Mg Alloys: Processing and Mechanical Properties

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

Tensile property and microstructure of Al−4.77Mn−1.37Mg−0.67Sc−0.25Zr alloy under different selective laser melting processing parameters

Selective laser melting of Al-3.48Cu-2.03Si-0.48Sc-0.28Zr alloy: Microstructure evolution, properties and metallurgical defects

Cracking Behavior, Microstructure and Properties of Selective Laser Melted Al-Mn-Mg-Sc-Zr Alloy

In-situ Investigation of the Anisotropic Mechanical Properties of Laser Direct Metal Deposition Ti6Al4V Alloy

Microstructural evolution and strengthening mechanism of high-strength AlSi8.1 Mg1.4 alloy produced by selective laser melting

Additive manufacturing of a high strength Al-5Mg2Si-2Mg alloy: Microstructure and mechanical properties

Thermal and mechanical properties of an Al-Mg-Sc-Zr high strength alloy fabricated by selective laser melting

Aging responses of an Al-Cu alloy fabricated by selective laser melting

Microstructure and mechanical properties of Al-Fe-Sc-Zr alloy additively manufactured by selective laser melting

Microstructure, metallurgical defects and hardness of Al–Cu–Mg–Li–Zr alloy additively manufactured by selective laser melting

Superior mechanical properties of a selective-laser-melted AlZnMgCuScZr alloy enabled by a tunable hierarchical microstructure and dual-nanoprecipitation

The mechanical and functional behaviors of Mn–15 wt.%Cu alloy produced by selective laser melting

Microstructures and tensile properties of a selective laser melted Al–Zn–Mg–Cu (Al7075) alloy by Si and Zr microalloying

Densification, microstructure and properties of Sc and Zr modified Al-Mn alloy prepared by selective laser melting

Microstructure and Mechanical Properties of an Er-Modified Al–Mg–Mn–Sc–Zr Alloy Processed by Selective Laser Melting

Selective laser melting processing of heterostructured Ti6Al4V/FeCoNiCrMo alloy with superior strength and ductility

Developing a high-strength Al-Mg-Si-Sc-Zr alloy for selective laser melting: Crack-inhibiting and multiple strengthening mechanisms

Achieving high strength in selective laser melting AlSi10Mg alloy by adding microsized pure Cu particles