Effect of Process Parameters and Heat Treatment on the Microstructure and Properties of CuCrZr Alloy by Selective Laser Melting
Qingjuan Wang,Yufeng Zhang,Kuaishe Wang,Shifeng Liu,Xi Zhang,Huijun Shao
DOI: https://doi.org/10.1016/j.msea.2022.144054
2022-01-01
Abstract:Complex CuCrZr alloy parts with well-matched conductivity and strength can be prepared by adjusting the process parameters of selective laser melting (SLM). Thus, in this study, SLM was used to prepare CuCrZr alloys, and their structure, electrical conductivity, and mechanical properties were analyzed. Moreover, effect of aging treatment on the alloy structure was investigated. With the laser power of 400 W, scanning speed of 300 mm/s, and scanning distance of 80 μm, an CuCrZr alloy sample with a maximum relative density of 99.15% and elongation of 71.7% was obtained by SLM. After direct age hardening (DAH) at 480 °C for 2 h, the conductivity and strength of the alloy increased significantly. In particular, the conductivity increased from 22.16%IACS to 72.8%IACS, indicating an overall increase of 228.5%. Meanwhile, the strength increased from 265.5 to 612.0 MPa. From the backscatter diffraction analysis, the small-angle grain boundaries increased after aging, and the crystal orientation changed from <101> to <111>. During direct aging, a large amount of nanoscale Cr phase was precipitated from the supersaturated solid solution, which increased the strength of the alloy. Further, precipitation strengthening was determined to be the main alloy strengthening mechanism. Moreover, the reduction in the solid solution content reduced the electron scattering effect and increased the overall conductivity of the alloy.