Thermal Stability of Encapsulated Carbon-Based Multiporous-Layered-Electrode Perovskite Solar Cells Extended to Over 5000 h at 85 °C

Ryuki Tsuji,Yuuma Nagano,Kota Oishi,Eiji Kobayashi,Seigo Ito
DOI: https://doi.org/10.3390/ma17123002
IF: 3.4
2024-06-20
Materials
Abstract:The key to the practical application of organometal–halide crystals perovskite solar cells (PSCs) is to achieve thermal stability through robust encapsulation. This paper presents a method to significantly extend the thermal stability lifetime of perovskite solar cells to over 5000 h at 85 °C by demonstrating an optimal combination of encapsulation methods and perovskite composition for carbon-based multiporous-layered-electrode (MPLE)-PSCs. We fabricated four types of MPLE-PSCs using two encapsulation structures (over- and side-sealing with thermoplastic resin films) and two perovskite compositions ((5-AVA)x(methylammonium (MA))1−xPbI3 and (formamidinium (FA))0.9Cs0.1PbI3), and analyzed the 85 °C thermal stability followed by the ISOS-D-2 protocol. Without encapsulation, FA0.9Cs0.1PbI3 exhibited higher thermal stability than (5-AVA)x(MA)1−xPbI3. However, encapsulation reversed the phenomenon (that of (5-AVA)x(MA)1−xPbI3 became stronger). The combination of the (5-AVA)x(MA)1−xPbI3 perovskite absorber and over-sealing encapsulation effectively suppressed the thermal degradation, resulting in a PCE value of 91.2% of the initial value after 5072 h. On the other hand, another combination (side-sealing on (5-AVA)x(MA)1−xPbI3 and over- and side-sealing on FA0.9Cs0.1PbI3) resulted in decreased stability. The FACs-based perovskite was decomposed from these degradation mechanisms by the condensation reaction between FA and carbon. For side-sealing, the space between the cell and the encapsulant was estimated to contain approximately 1,260,000 times more H2O than in over-sealing, which catalyzed the degradation of the perovskite crystals. Our results demonstrate that MA-based PSCs, which are generally considered to be thermally sensitive, can significantly extend their thermal stability after proper encapsulation. Therefore, we emphasize that finding the appropriate combination of encapsulation technique and perovskite composition is quite important to achieve further device stability.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The paper aims to address the thermal stability issues faced by perovskite solar cells (PSCs) in practical applications. Specifically, the authors attempt to significantly extend the thermal stability lifetime of carbon-based mesoporous layer electrode (MPLE) PSCs by optimizing the combination of encapsulation methods and perovskite compositions. The paper demonstrates how the optimal encapsulation techniques and perovskite composition combinations can achieve a thermal stability lifetime of over 5000 hours for perovskite solar cells under conditions of 85°C. Four different types of MPLE-PSCs were prepared in the study, employing two encapsulation structures (top encapsulation and side encapsulation) and two different perovskite compositions ((5-AVA)x(MA)1-xPbI3 and (FA)0.9(Cs)0.1PbI3). The results showed that, without encapsulation, (FA)0.9(Cs)0.1PbI3 exhibited higher thermal stability compared to (5-AVA)x(MA)1-xPbI3; however, after encapsulation, this phenomenon was reversed, with (5-AVA)x(MA)1-xPbI3 demonstrating stronger thermal stability. In particular, the combination of the (5-AVA)x(MA)1-xPbI3 absorber and top encapsulation technique effectively suppressed thermal degradation, maintaining 91.2% of the initial power conversion efficiency (PCE) after 5072 hours. On the other hand, other combinations (side encapsulation of (5-AVA)x(MA)1-xPbI3 and both top and side encapsulation of (FA)0.9(Cs)0.1PbI3) resulted in decreased stability. Additionally, the study found that the H2O content in the side encapsulation space was approximately 1,260,000 times higher than in the top encapsulation, which catalyzed the degradation of perovskite crystals. Therefore, the study emphasizes the importance of finding suitable combinations of encapsulation techniques and perovskite compositions to further enhance device stability.