Abstract:In this work, a novel TiC nanoparticle (0.5 wt %) reinforced Mg-2.9Zn-1.1Ca-0.5Mn nanocomposite, with a mixed grain microstructure exhibiting high strength and targeted for biocompatible/structural applications was successfully prepared by ultrasonic assisted semi-solid stirring and extrusion at ultra-slow speeds of 1, 0.1 and 0.01 mm/s. The experimental results revealed that the morphology of the eutectic Ca2Mg6Zn3 phase in the as-cast nanocomposite changed from plate-like to lamellar as a low mass fraction of TiCp was added. Both dynamically recrystallized grains and precipitates were gradually refined with decreasing extrusion speed. The finest recrystallized grains (similar to 0.46 mu m), with a high volume fraction (similar to 4.3%) of fine precipitates, appeared after extrusion at 0.01 mm/s. The refined grain structure was not only due to dynamic recrystallization, but also the synergistic pinning effects from nano-TiCp as well as precipitated MgZn2 and alpha-Mn particles. The superior ultimate tensile strength (similar to 410.3 MPa), yield strength (similar to 384.5 MPa) and elongation to failure (similar to 4%) were obtained in the nanocomposite extruded at the slowest speed (0.01 mm/s) and had the potential to serve as a candidate material in orthopaedic applications. The improved strength was mainly related to grain refinement, thermal expansion effects and Orowan strengthening. Grain refinement, in particular, contributed to the largest strengthening increment. High tensile toughness of similar to 66.6 KJ mm(-3) was achieved for the nanocomposite extruded at a speed of 1 mm/s. Further, it exhibited a high strain hardening rate, theta, at stage IV. The fracture surface exhibited abundant dimples and consistent with high ductility. Remnant coarse Ca2Mg6Zn3 particles acted as crack initiators under high applied stress in tension, leading to structural failure.

High Strength TiCp/Mg-Zn-Ca Magnesium Matrix Nanocomposites with Improved Formability at Low Temperature

Microstructure and Mechanical Properties of TiCp/Mg-4Zn-0.5Ca Nanocomposite in Different Processing Conditions

Microstructure and Mechanical Properties of Ultra-High Strength TiCp/Mg-1.4Zn-2.6Ca-0.5Mn Nanocomposite after Hot Extrusion

Effect of extrusion temperature on microstructure and mechanical properties of a low-alloying and ultra-high strength Mg–Zn–Ca–Mn matrix composite containing trace TiC nanoparticles

Effect of Extrusion Speed on Mixed Grain Microstructure and Tensile Properties of a Mg-2.9Zn-1.1Ca-0.5Mn Nanocomposite Reinforced by a Low Mass Fraction of TiCp

Effect of Extrusion on the Microstructure and Mechanical Properties of a Low-Alloyed Mg−2Zn−0.8Sr−0.2Ca Matrix Composite Reinforced by TiC Nano-Particles

Microstructure and tensile properties of magnesium matrix nanocomposite reinforced by high mass fraction of nano-sized particles including TiC and MgZn<sub>2</sub>

Microstructure and mechanical properties of TiC nanoparticle-reinforced Mg−Zn−Ca matrix nanocomposites processed by combining multidirectional forging and extrusion

Fabrication of Biodegradable Magnesium Matrix Composite with Ultrafine Grains and High Strength by Adding TiC Nanoparticles to Mg-1.12Ca-0.84Zn-0.23Mn (at.%) Alloy.

Microstructures and Enhanced Mechanical Properties of (Zr, Ti)(C, N)-Based Nanocomposites Fabricated by Reactive Hot-Pressing at Low Temperature

Ultrahigh Strength TiCnp/Mg–2Zn-0.8Sr-0.2Ca Magnesium Matrix Composite Processed by Combining Multidirectional Forging with Extrusion

Microstructure and Tensile Strength of Nano-TiCp/Mg–Zn–Ca Magnesium Matrix Nanocomposites Processed by Multidirectional Forging

Work Hardening and Softening Behavior of Mg–Zn–Ca Alloy Influenced by Deformable Ti Particles

Influence of Extrusion Temperature and Process Parameter on Microstructures and Tensile Properties of a Particulate Reinforced Magnesium Matrix Nanocomposite

Simultaneous Improvements in Tensile Strength and Elongation of a Mg-2Zn-0.8Sr-0.2Ca Alloy by a Combination of Microalloying and Low Content of TiC Nanoparticles

Microstructures, Tensile Properties and Work Hardening Behavior of SiCp/Mg-Zn-Ca Composites

Simultaneously Increasing the High-Temperature Tensile Strength and Ductility of Nano-Sized TiCp Reinforced Al-Cu Matrix Composites

Effect of Hot Extrusion on Microstructures and Mechanical Properties of SiC Nanoparticles Reinforced Magnesium Matrix Composite

Simultaneously Increasing the Elevated-Temperature Tensile Strength and Plasticity of in Situ Nano-Sized TiCx/Al-Cu-Mg Composites

Improvement of Strength and Ductility of TC4p/AZ91D Magnesium Matrix Composites by Modifying the Extrusion Ratio