Microstructure and tensile properties of magnesium matrix nanocomposite reinforced by high mass fraction of nano-sized particles including TiC and MgZn<sub>2</sub>

Kai-bo Nie,Ya-chao Guo,Paul Munroe,Kun-kun Deng,Xin-kai Kang
DOI: https://doi.org/10.1016/j.jallcom.2019.153348
IF: 6.2
2020-01-01
Journal of Alloys and Compounds
Abstract:A low mass fraction of TiC nanoparticles was successfully introduced into a Mg-4Zn-0.5Ca matrix alloy using mechanical stirring together with ultrasonic treatment. As the mass fraction of TiC nanoparticles increased, the grain size of the matrix was gradually reduced, while the concentrations of the MgZn and Ca2Mg6Zn second phase particles were decreased. This indicated that the externally applied TiC nanoparticles could refine the matrix grains and retard the formation of MgZn and Ca2Mg6Zn3 during solidification. The introduction of the TiC nanoparticles and the precipitation of nano-sized MgZn2 contributed to the refined recrystallized grains after low temperature slow-speed extrusion. The total volume fraction of the nano-sized reinforcement consisted of TiC nanoparticles and nano-sized precipitates MgZn2 was more than 3%, which was higher than in previously developed magnesium matrix nanocomposites. The yield strength, ultimate tensile strength and elongation of the as-extruded 1 wt% nanocomposite were 369.8 MPa, 393.6 MPa and 6.7%, respectively. This excellent tensile strength was mainly associated with high mass fraction of nano-sized precipitates as well as the added TiC nanoparticles. (C) 2019 Elsevier B.V. All rights reserved.
What problem does this paper attempt to address?