Mechanical properties and fabrication of carbon nanotubes reinforced AZ91D magnesium matrix nanocomposites

Congyang Zhang,Wenzhen Li,Yu Jin,Weidong Xue,Weiming Gao

2013-01-01

Abstract:Carbon nanotubes (CNTs) reinforced AZ91D magnesium matrix nanocomposites were fabricated by mechanical stirring combined with ultrasonic vibration dispersion. Microstructure and mechanical properties of CNTs/AZ91D composites were investigated by optical metallographic microscope (OM), scanning electronic microscope (SEM) and tensile test, and fracture morphology of the tensile samples was also observed by SEM and energy spectrum analysis (EDS). The results show that carbon nanotubes can be added smoothly and distributed dispersedly in the AZ91D magnesium matrix alloy by the semi-solid mechanical stirring and high-energy ultrasonic treatment. When CNTs addition is in range of 0~1.0%, with the increase of CNTs content, tensile strength and elongation of the composites prepared are improved obviously. Tensile strength, yield strength and elongation of 1.0% CNTs /AZ91D magnesium matrix composites reach 200 MPa, 114 MPa and 5.4%, respectively, compared with those of matrix alloy, increased by 51.5%, 42.5% and by 170%, respectively, showing excellent comprehensive mechanical properties. Carbon nanotubes mainly play the role in refining grains of the nanocomposites and bearing deformation loading.