Abstract:In the present paper, the ZrB2/h-BN multiphase ceramics were fabricated by SPS (spark plasma sintering) technology at lower sintering temperature using h-BN, ZrO2, AlN and Si as raw materials and B2O3 as a sintering aid. The phase constitution and microstructure of specimens were analyzed by XRD and SEM. Moreover, the effects of different sintering pressures on the densification, microstructure and mechanical properties of ZrB2/h-BN multiphase ceramics were also systematically investigated. The results show that the ZrB2 was obtained through solid phase reaction at different sintering pressures, and increasing sintering pressure could accelerate the formation of ZrB2 phase. As the sintering pressure increasing, the fracture strength and toughness of the sintered samples had a similar increasing tendency as the relative density. The better comprehensive properties were obtained at given sintering pressure of 50MPa, and the relative density, fracture strength and toughness reached about 93.4%, 321MPa and 3.3MPa·m1/2, respectively. The SEM analysis shows that the h-BN grains were fine and uniform, and the effect of sintering pressure on grain size was inconspicuous. The distribution of grain is random cross array, and the fracture texture was more obvious with the increase of sintering pressure. The fracture mode of sintered samples remained intergranular fracture mechanism as sintering pressure changed, and the grain refinement, grain pullout and crack deflection helped to increase the mechanical properties.

Densification Behavior and Mechanical Properties of Spark Plasma Reaction Sintered ZrB2–ZrC-B4C Ceramics from B4C-Zr System

Processing and Mechanical Properties of Zirconium Diboride‐Based Ceramics Prepared by Spark Plasma Sintering

In Situ ZrB2 Formation in B4C Ceramics and Its Strengthening Mechanism on Mechanical Properties

Densification mechanism, microstructure and mechanical properties of ZrC ceramics prepared by high-pressure spark plasma sintering

Effect of Nano SiC on Microstructure and Mechanical Properties of BN-ZrO2-SiC Multiphase Ceramics

Effects of SiC Platelet and ZrSi2 Additive on Sintering and Mechanical Properties of ZrB2-based Ceramics by Hot-Pressing

SPS Sintering Behavior and Microstructure of ZrB2-SiCpl Composite Ceramics

Microstructure and mechanical properties of SiC composite ceramics modified by (TixZr1–x)B2 solid solution

Densification and strengthening mechanism in spark plasma sintering of B4C–VB2 ceramics via carbide boronizing

The Fabrication and Mechanical Properties of SiC/ZrB2 Laminated Ceramic Composite Prepared by Spark Plasma Sintering

Preparation and Mechanical Properties of Laminated Zirconium Diboride/molybdenum Composites Sintered by Spark Plasma Sintering

Toughening mechanism of B4C/TiB2 ceramic materials by in situ reaction via spark plasma sintering

Microstructure and mechanical properties of spark plasma sintered SiC ceramics aided by B4C

Processing and mechanical properties of B4C-SiCw ceramics densified by spark plasma sintering

Spark plasma sintering and hot pressing of ZrB2–SiCW ultra-high temperature ceramics

SPS densification and ablative performance of ZrB2–SiC–ZrC composites derived from the ternary powders by sol-gel

Microstructure and Mechanical Properties of ZrB2/h-BN Multiphase Ceramics by Low-Temperature Reactive Sintering

Preparation of dense B4C ceramics by spark plasma sintering of high-purity nanoparticles

Microstructures and mechanical properties of reactive spark plasma-sintered ZrB2–SiC–MoSi2 composites

Influence of TiB2 and CrB2 on densification, microstructure, and mechanical properties of ZrB2 ceramics

Microstructure and mechanical properties of pressure‐less sintered B4C–SiC–ZrB2–LaB6 ceramic composites