Abstract:The radiation-induced segregation (RIS) and microstructure evolution such as dislocation loops and cavities are major microstructural causes for the irradiation-assisted stress corrosion cracking (IASCC) of austenitic stainless steel (SS) core components. While a couple of studies have been reported on the irradiation induced damage in nuclear grade (NG) austenitic SS, the evolution of dislocation loop density and size and its correlation with the mechanical properties have still remained incompletely understood. In addition, the correlation between the segregation at the grain boundary and that at the dislocation loop has received limited attentions. In particular, there is still a lack of a systematic study of the irradiation damage in domestically fabricated NG austenitic SS. In this work, the proton-irradiation induced microstructural damage in domestically fabricated 304NG SS was characterized, in an effort to correlate the RIS and the dislocation loop density and size with the irradiation dose, as well as the dislocation loop density and size with the radiation-induced hardening. The results revealed that the radiationinduced microstructure damage was mainly dislocation loops with a few micro-voids. The loop density was in the order of 10(22) m(-3) with an average size of <10 nm. The square root of the product of loop density and size (Nd)(0.5), scaled linearly with the square root of irradiation dose with a factor of 6.8x10(3) dpa(-0.5) . mm(-1). The loops were believed to be mainly responsible for the hardening in 304NG SS, which also scaled linearly with (Nd)(0.5) with a factor of 1.16x10(-2) HV0.025 . mm. A comparative analysis about the segregation at the grain boundary and at the dislocation loop was conducted. While the depletion of Cr and enrichment of Ni at the dislocation loop and grain boundary showed no difference, the enrichment of Si at the dislocation loop could be of about 6 times of that at the grain boundary. In addition, the loop density and loop size, as well as RIS and radiation-induced hardening were all increased by a higher dose and tended to saturate by a dose of 3.0 similar to 5.0 dpa.

Irradiation-induced Precipitation and Inverse Coarsening of G-phase in Austenitic Stainless Steel Weld Metal

Irradiation-induced Segregation at Phase Boundaries in Austenitic Stainless Steel Weld Metal

Modified microstructures in proton irradiated dual phase 308L weldment filler material

Interactive Effect of Thermal Aging and Proton Irradiation on Microstructural Evolution and Hardening of Δ-Ferrite in 308L Stainless Steel Weld Metal

Effect of Post-Irradiation Annealing on Microstructure and Corrosion of Proton-Irradiated 308L Stainless Steel Weld Metal

Irradiation-induced Grain Growth in Nanocrystalline Reduced Activation Ferrite/martensite Steel

Corrosion of Phase and Phase Boundary in Proton-Irradiated 308L Stainless Steel Weld Metal in Simulated PWR Primary Water

Interactive Effect of Thermal Aging and Proton Irradiation on Microstructural Evolution and Hardening of 8-Ferrite in 308L Stainless Steel Weld Metal

Study of Irradiation Damage in Domestically Fabricated Nuclear Grade Stainless Steel

Proton Irradiation Effects on the Electron Work Function, Corrosion and Hardness of Austenitic Stainless Steel Phases

Deformation and Cracking Behaviors of Proton-Irradiated 308L Stainless Steel Weld Metal Strained in Simulated PWR Primary Water

Irradiation-induced corrosion tendencies evolution at the phase boundaries containing carbides in duplex stainless steel

Microstructure evolution and lead-bismuth eutectic corrosion behavior of 11Cr1Si ferritic/martensitic steel after proton irradiation

Precipitation behavior in G-phase strengthened ferritic stainless steels

Investigation of Nano-Scale Segregation in Nanostructured Ferritic Alloy 14YWT after Heavy Ion Irradiation

Si promotes nano-clusters and α phase separation in early-stage neutron irradiated low activation ferritic/martensitic steel

Microstructure evolution and void swelling of ODS ferritic/martensitic steel under high damage irradiation

Irradiation-induced segregation/desegregation at grain boundaries of a ferritic Fe-Mn-Si steel

Formation of Ni-Si clusters and their relationship with dislocation loops in irradiated stainless steels

Effect of Irradiation on Austenite Phase in Thermally Aged 308 Stainless Steel Weld Metal

High-energy synchrotron x-ray study of deformation-induced martensitic transformation in a neutron-irradiated Type 316 stainless steel